A new nanoparticle penetrant used for plasma electrolytic oxidation film coated on AZ31 Mg alloy in service environment

被引:24
作者
Guo, Xinghua [1 ]
Du, Keqin [1 ,2 ]
Wang, Yanqiu [2 ]
Shao, Yawei [2 ]
Wang, Fuhui [1 ]
机构
[1] Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang, Peoples R China
[2] Harbin Engn Univ, Coll Mat Sci & Chem Engn, Harbin, Peoples R China
关键词
Self-assembled nanophase particle; Plasma electrolytic oxidation; Service environment; AZ31 Mg alloy; Corrosion; AZ91D MAGNESIUM ALLOY; ELECTROCHEMICAL CORROSION BEHAVIOR; ACID CONVERSION COATINGS; SNAP SURFACE TREATMENTS; PROTECTION; RESISTANCE; MICROSTRUCTURE; COMPOSITE;
D O I
10.1016/j.surfcoat.2012.05.063
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
A new penetrant of improved self-assembled nanophase particle (SANP) solution was used to protect AZ31 Mg alloy with plasma electrolytic oxidation (PEO) film in the service environment. The improved SANP technique was carried out by increasing water concentration, prolonging hydrolytic time, reducing solution acidity and adding phytic acid (PAH) inhibitor. Properties of the improved SANP solution and the PEO + SANP film were evaluated by transmission electron microscopy (TEM), scanning electron microscopy (SEM) and potentiodynamic polarization. Service performance of the PEO + fluorocarbon (FC) paint treated by the improved SANP technique was estimated by thermal shock method (TSM) and neutral salt spray test (NSST). Experiment results indicated that permeability of the improved SANP solution was increased obviously due to the formation of smaller nanoparticles. Uniformity and corrosion protection of the PEO + improved SANP film were further enhanced attributed to the restriction in the formation of bigger inorganic particles and the stability of the PAH inhibitor, respectively. For the composite film of PEO film + improved SANP + FC, it still had strong adhesion and good corrosion protection after the service environment tests of TSM and NSST due to the chemical combinations of SANP/PEO and SANP/FC. (C) 2012 Elsevier B.V. All rights reserved.
引用
收藏
页码:4833 / 4839
页数:7
相关论文
共 26 条
[1]  
[Anonymous], B11707 ASTM
[2]  
[Anonymous], 1996, 165361996 GBT
[3]  
[Anonymous], 46242002 ISO
[4]   Growth regularity of ceramic coating on magnesium alloy by plasma electrolytic oxidation [J].
Chang, Limin .
JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 468 (1-2) :462-465
[5]   Influence of phytic acid concentration on performance of phytic acid conversion coatings on the AZ91D magnesium alloy [J].
Cui, Xiufang ;
Li, Ying ;
Li, Qingfen ;
Jin, Guo ;
Ding, Minghui ;
Wang, Fuhui .
MATERIALS CHEMISTRY AND PHYSICS, 2008, 111 (2-3) :503-507
[6]   Microstructure and corrosion resistance of phytic acid conversion coatings for magnesium alloy [J].
Cui, Xiufang ;
Li, Qingfen ;
Li, Ying ;
Wang, Fuhui ;
Jin, Guo ;
Ding, Minghui .
APPLIED SURFACE SCIENCE, 2008, 255 (05) :2098-2103
[7]   Self-assembled NAnophase Particle (SNAP) surface treatments for corrosion protection of AA2024-T3 [J].
Donley, MS ;
Balbyshev, VN ;
Voevodin, NN .
PROGRESS IN ORGANIC COATINGS, 2005, 52 (01) :34-38
[8]   The self-assembled nanophase particle (SNAP) process: a nanoscience approach to coatings [J].
Donley, MS ;
Mantz, RA ;
Khramov, AN ;
Balbyshev, VN ;
Kasten, LS ;
Gaspar, DJ .
PROGRESS IN ORGANIC COATINGS, 2003, 47 (3-4) :401-415
[9]   Phytic acid conversion coating on Mg-Li alloy [J].
Gao, Lili ;
Zhang, Chunhong ;
Zhang, Milin ;
Huang, Xiaomei ;
Jiang, Xi .
JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 485 (1-2) :789-793
[10]   Protective coatings on magnesium and its alloys - a critical review [J].
Gray, JE ;
Luan, B .
JOURNAL OF ALLOYS AND COMPOUNDS, 2002, 336 (1-2) :88-113