Temperature dependence of charge packet velocity in XLPE cable peelings

The generation and transit of charge packets in 150 mu m thick peelings from the insulation of Medium Voltage Cables manufactured using the same XLPE batch have been investigated at a number of different temperatures. Charge packet motion was investigated in peelings taken from cables that have been electro-thermally stressed at T= 90 degrees C for 5000 hours with a Laplacian field E approximate to 20kV/mm at the location of the samples. It was found that charge packets were generated by an applied field of 120kV/mm when the internal space charge field reached 140-150kV/mm. Measurements were made in three controlled temperature environments and it was found that the transit time fitted an Arrhenius; behaviour with an activation energy of similar to 1.2 eV. This value is similar to estimates made for the deepest traps (> 1.1eV) made from the decay of space charge accumulated at lower fields of 46.67kVmm. It is also close to the activation energy for the conductivity (degrees similar to 1.25 eV) obtained from the dielectric spectroscopy of unpeeled cable sections at Er-rms approximate to V/mm, and similar to 1.15eV from the dielectric spectroscopy of the peelings (E = 40V/mm). It is therefore concluded that the transit of the charge packet is associated with the trap-to-trap transport of charge carriers located in the deepest traps available. The implications of these results for the mechanism of charge packet generation is discussed.