Comparative corrosion behavior of Zn with Fe and Mg in the course of immersion degradation in phosphate buffered saline

被引：128

作者：

Chen, Yingqi ^{[1
]}

Zhang, Wentai ^{[1
]}

Maitz, Manfred F. ^{[1
,2
]}

Chen, Meiyun ^{[1
]}

Zhang, Heng ^{[1
]}

Mao, Jinlong ^{[1
]}

Zhao, Yuancong ^{[1
]}

Huang, Nan ^{[1
]}

Wan, Guojiang ^{[1
]}

机构：

[1] Southwest Jiaotong Univ, Coll Mat Sci & Engn, Key Lab Adv Technol Mat, Minist Educ, Chengdu 61003, Peoples R China

[2] Max Bergmann Ctr Biomat, Leibniz Inst Polymer Res Dresden, Hohe Str 06, D-01069 Dresden, Germany

来源：

CORROSION SCIENCE | 2016年 / 111卷

基金：

中国国家自然科学基金;

关键词：

Zinc; Iron; Magnesium; Oxygen reduction; Pitting corrosion; Kinetic parameters; BIODEGRADABLE MAGNESIUM IMPLANTS; IN-VITRO DEGRADATION; PITTING CORROSION; PURE IRON; ALLOYS; ZINC; OXIDATION; STENTS; RESISTANCE; COATINGS;

D O I：

10.1016/j.corsci.2016.05.039

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The corrosion behavior of Zn was compared with those of Fe and Mg in a long-term course of immersing in phosphate buffered saline (PBS) as biodegradable metal for bio-implants application. The comparison focused on corrosion rate, mode, products and surface characteristics along the immersion degradation up to 21 days. For transient assays, the open circuit potential and corrosion rate placed Zn between Fe and Mg. However, in a long-term course the corrosion rate of Zinc developed faster than Fe and Mg. This was ascribed to its unique localized corrosion and corrosion products changing in contrast to Fe and Mg. (C) 2016 Elsevier Ltd. All rights reserved.

引用

页码：541 / 555

页数：15

共 50 条

[31] Corrosion and degradation decelerating alendronate embedded zinc phosphate hybrid coating on biodegradable Zn biomaterials
Mo, Xiaoshan
Qian, Junyu
Chen, Yingqi
Zhang, Wentai
Xian, Peng
Tang, Shuai
Zhou, Chao
Huang, Nan
Ji, Huanzhong
Luo, En
Zhang, Haijun
Wan, Guojiang
CORROSION SCIENCE, 2021, 184
[32] In vitro degradation of poly(L-lactic acid) fibers in phosphate buffered saline
Yuan, XY
Mak, AFT
Yao, KD
JOURNAL OF APPLIED POLYMER SCIENCE, 2002, 85 (05) : 936 - 943
[33] Characterization of accelerated hydrolysis degradation of poly (lactic acid) in phosphate buffered saline solution
Woo, Soo-Hyun
Wee, Jung-Wook
POLYMER DEGRADATION AND STABILITY, 2024, 223
[34] Comparative Study on Corrosion Behavior and Mechanism of As-Cast Mg-Zn-Y and Mg-Zn-Gd Alloys
Xi, Guoqiang
Zhao, Xuhan
Ma, Yanlong
Mou, Yu
Xiong, Ju
Ma, Kai
Wang, Jingfeng
ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2023, 36 (02): : 310 - 322
[35] Corrosion behavior of a non vascular, double-layer, surgical esophageal nitinol stent in phosphate-buffered saline solution
Kim, Y-S
Ki, J-G
SELECTED PROCEEDINGS FROM THE 232ND ECS MEETING, 2017, 80 (10): : 487 - 497
[36] Effect of Ca and Mn on Corrosion Behavior of Mg-Zn Alloys in Phosphate Buffer Solution
Ding Yutian
Shen Yue
Zhang Hongfei
Lei Jian
Li Ruimin
Gao Yubi
RARE METAL MATERIALS AND ENGINEERING, 2022, 51 (08) : 3031 - 3040
[37] Investigation of the Corrosion Behavior of Zn-Al-Mg Hot-Dip Galvanized Steel in Alternating Climate Tests
Keppert, T. A.
Luckeneder, G.
Stellnberger, K. -H.
Mori, G.
Antrekowitsch, H.
CORROSION, 2014, 70 (12) : 1238 - 1248
[38] Corrosion degradation behavior of Mg-Ca alloy with high Ca content in SBF
Liu, Yi-chi
Liu, De-bao
Zhao, Yue
Chen, Min-fang
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2015, 25 (10) : 3339 - 3347
[39] Corrosion behaviour of niobium in phosphate buffered saline solutions with different concentrations of bovine serum albumin
Wang, Wei
Mohammadi, Farzad
Alfantazi, Akram
CORROSION SCIENCE, 2012, 57 : 11 - 21
[40] Localized corrosion behavior associated with Al7Cu2Fe intermetallic in Al-Zn-Mg-Cu-Zr alloy
Sun, Yuanwei
Pan, Qinglin
Sun, Yuqiao
Wang, Weiyi
Huang, Zhiqi
Wang, Xiangdong
Hu, Quan
JOURNAL OF ALLOYS AND COMPOUNDS, 2019, 783 : 329 - 340

← 1 2 3 4 5 →