Effect of Nanocrystalline TiB2 Addition on Properties of Copper Powder Reinforced Epoxy Composites

被引：9

作者：

Chary, V. Rangadhara ^{[1
]}

Rao, T. Srinivasa ^{[2
]}

Mohan, M. K. ^{[1
]}

机构：

[1] NIT Warangal, Dept MME, Warangal, Telangana, India

[2] NIT Tiruchirappalli, Dept MME, Tiruchirappalli, Tamil Nadu, India

来源：

TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS | 2017年 / 70卷 / 10期

关键词：

Epoxy nanocomposites; Nanocrystalline SHS TiB2; Glass transition temperature; Mechanical properties; XRD; SEM; TEM; MECHANICAL-PROPERTIES; THERMAL-PROPERTIES; NANOCOMPOSITES; BEHAVIOR;

D O I：

10.1007/s12666-017-1130-x

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The present investigation aims at understanding the influence of nanocrystalline TiB2 powder on thermal and mechanical properties of Epoxy-Cu microcomposites. The nanocrystalline TiB2 powder has been synthesized by SHS and the particle size is in the range of 60-70 nm as revealed from TEM studies. The Epoxy-Cu microcomposites are casted using hand-layout technique and cured under vacuum at room temperature. The nanocomposites have been prepared by addition of 0.2, 0.4, 0.6, 0.8, and 1.0 vol% TiB2 to Epoxy-4 vol% Cu microcomposite. Ductility has increased by 3-4 times in comparison to neat epoxy, and it has increased by 2-3 times in comparison to microcomposites. The Vickers hardness of composites shows an increasing trend with increasing particulate content. XRD studies show the intensity of amorphous epoxy phase decreasing with increasing filler content. The SEM micrographs show a uniform and dispersed distribution of Cu particles in the epoxy matrix. DSC studies reveal the glass transition temperature, T-g, of the epoxy composites to be higher than the neat epoxy and a decreasing trend is observed with increasing filler content.

引用

页码：2695 / 2706

页数：12

共 25 条

[1] Experimental investigation of micro-sized aluminium oxide reinforced epoxy composites for microelectronic applications [J].

Agrawal, Alok ;

Satapathy, Alok .

INTERNATIONAL CONFERENCE ON ADVANCES IN MANUFACTURING AND MATERIALS ENGINEERING (ICAMME 2014), 2014, 5 :517-526

[2] A review of vapor grown carbon nanofiber/polymer conductive composites [J].

Al-Saleh, Mohammed H. ;

Sundararaj, Uttandaraman .

CARBON, 2009, 47 (01) :2-22

[3] Influence of Fe/Ni/Al additive on the sintering behaviors of TiB2 cermets [J].

Chen Hua ;

Zhang Jinyong ;

Fu Zhengyi .

JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2009, 24 (06) :879-882

[4] CRAZING AND SHEAR DEFORMATION IN GLASS BEAD-FILLED GLASSY-POLYMERS [J].

DEKKERS, MEJ ;

HEIKENS, D .

JOURNAL OF MATERIALS SCIENCE, 1985, 20 (11) :3873-3880

[5]

Gadakary S, 2015, THESIS

[6] Production of nanocrystalline TiB2 powder through self-propagating high temperature synthesis (SHS) of TiO2-H3BO3-Mg mixture [J].

Gadakary, Saikumar ;

Khanra, Asit K. ;

Veerabau, R. .

ADVANCES IN APPLIED CERAMICS, 2014, 113 (07) :419-426

[7]

Guo Q, 2012, WOODHEAD PUBL MATER, P1, DOI 10.1533/9780857097637

[8] Study of mechanical properties of epoxy/glass/nanoclay hybrid composites [J].

Karippal, Jeena Jose ;

Murthy, H. N. Narasimha ;

Rai, K. S. ;

Sreejith, M. ;

Krishna, M. .

JOURNAL OF COMPOSITE MATERIALS, 2011, 45 (18) :1893-1899

[9] Fracture toughness of the nano-particle reinforced epoxy composite [J].

Kim, Byung Chul ;

Park, Sang Wook ;

Lee, Dai Gil .

COMPOSITE STRUCTURES, 2008, 86 (1-3) :69-77

[10] Positive temperature coefficient behavior of polymer composites having a high melting temperature [J].

Kim, JI ;

Kang, PH ;

Nho, YC .

JOURNAL OF APPLIED POLYMER SCIENCE, 2004, 92 (01) :394-401

← 1 2 3 →