The effect of sintering activator on the erosion behavior of infiltrated W-10wt%Cu composite

被引：29

作者：

Borji, S. ^{[1
]}

Ahangarkani, M. ^{[1
]}

Zangeneh-Madar, K. ^{[1
]}

Valefi, Z. ^{[1
]}

机构：

[1] Malek Ashter Univ Technol, Dept Mat, Tehran 158751774, Iran

来源：

INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS | 2017年 / 66卷

关键词：

Infiltrated W-Cu composite; Activator; Erosion; Transpiration cooling; SOLID PARTICLE EROSION; NICKEL-DOPED TUNGSTEN; CU COMPOSITES; TEMPERATURE; REDUCTION; PRESSURE; POWDER; COPPER; CO;

D O I：

10.1016/j.ijrmhm.2017.03.007

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this paper, the erosion mechanism of infiltrated W-10wt%Cu composites against liquid alumina particles as well as the effect of sintering activators was studied. The fabrication of samples consists of infiltration of copper into sintered porous tungsten skeleton in presence of activators such as Ni and Co. Ni and Co was used as solid state sintering activators. The erosion of prepared specimens observed after the static firing and explained in terms of microstructure, transpiration cooling and erosion mechanism. Chemical analysis of the material after erosion test was obtained using energy dispersive X-ray analysis (EDS). SEM images were employed to identify the microstructure evolution due to erosion. The obtained results show that Composite prepared by Ni additive show about 33% better erosion resistance compare to specimen without additive. Also, presence of sintering activator could enhance transpiration cooling mechanism during erosion. These results discussed based on hardness, contiguity and connectivity. (C) 2017 Published by Elsevier Ltd.

引用

页码：150 / 157

页数：8

共 33 条

[1] The effect of additive and sintering mechanism on the microstructural characteristics of W-40Cu composites [J].

Ahangarkani, M. ;

Borgi, S. ;

Abbaszadeh, H. ;

Rahmani, A. A. ;

Zangeneh-Madar, K. .

INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2012, 32 :39-44

[2]

Ahangarkani M., 2014, J MAT SCI ENG, V11, P48

[3] The effect of compressing pressure on the microstructure and properties of W-10 wt.% Cu composite [J].

Ahangarkani, Meysam ;

Borgi, Saeid ;

Zageneh-madar, Karim ;

Valefi, Ziea .

INTERNATIONAL JOURNAL OF MATERIALS RESEARCH, 2015, 106 (10) :1046-1052

[4]

Aquaro D, 2001, MECCANICA, V36, P651, DOI 10.1023/A:1016396719711

[5]

Aquaro D., 2010, J MECH ENG, V56, P275

[6]

Bitter J.G.A., 1963, WEAR, V6, P5, DOI [10.1016/, DOI 10.1016/0043-1648(63)90003-6, 10.1016/0043-1648(63)90003-6]

[7] LIQUID-PHASE SINTERING OF HIGH-SPEED STEELS [J].

BOLTON, JD ;

GANT, AJ ;

HAGUE, RJM .

JOURNAL OF MATERIALS SCIENCE, 1991, 26 (19) :5203-5211

[8] Effects of low-content activators on low-temperature sintering of tungsten [J].

Boonyongmaneerat, Yuttanant .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2009, 209 (08) :4084-4087

[9]

Callister W. D., 1978, FUNDAMENTALS MAT SCI, P165

[10] Wear modes in slurry jet erosion of tungsten carbide hardmetals: Their relationship with microstructure and mechanical properties [J].

Gant, A. J. ;

Gee, M. G. .

INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2015, 49 :192-202

← 1 2 3 4 →