Formation of Al-based amorphous/nanocrystalline coatings by cold spraying

被引：19

作者：

Sun, Chengchuan ^{[1
]}

Zhou, Xianglin ^{[1
]}

Xie, Chen ^{[1
]}

Xu, Lingling ^{[1
]}

Li, Ruizhi ^{[1
]}

Liu, Binbin ^{[1
]}

机构：

[1] Univ Sci & Technol Beijing, State Key Lab Adv Met & Mat, Beijing 100083, Peoples R China

来源：

SURFACE & COATINGS TECHNOLOGY | 2020年 / 389卷

基金：

中国国家自然科学基金;

关键词：

Al-based amorphous/nanocrystalline coating; Cold spraying; Crystallization; Deposition process; Numerical simulation; METALLIC-GLASS COATINGS; DEFORMATION; BEHAVIOR; MICROSTRUCTURE; TEMPERATURE; PARTICLES; FLOW;

D O I：

10.1016/j.surfcoat.2020.125644

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Al-based amorphous/nanocrystalline coatings were prepared by cold spraying. The microstructures and microhardness of the coatings were investigated. The single particle's deposition was prepared and the formation of coatings was discussed. The amorphous content decreased with increased preheating temperature. The main crystalline phase was alpha-Al at preheating temperatures below 400 degrees C, with the appearance of other crystalline phases at 440 degrees C. The porosity values remained in the 3-4% range at different preheating temperatures and the microhardness of coatings decreased as the amorphous content declined. Analysis of the single particle's morphology revealed no obvious jet splashing and some particles at the interface retained near-spherical shape due to inhomogeneous deformation. The interaction of particles with the deposited coatings revealed the importance of alpha-Al because the alpha-Al could promote deformation to some extent. Then three types of interactions of particles with the deposited coatings were put forward. The simulation results about the two particles' interaction confirmed the effect of alpha-Al phase on the coating formation.

引用

页数：10

共 50 条

[11] Preparation of Al-based amorphous coatings and their properties
Jin, Lei
Zhang, Le
Liu, Kaige
Che, Zhigang
Li, Kai
Zhang, Ming
Zhang, Bo
JOURNAL OF RARE EARTHS, 2021, 39 (03) : 340 - 347
[12] STUDY ON Al-BASED AMORPHOUS AND NANOCRYSTALLINE COMPOSITE COATING
Lang Xiubing
Zhang Zhibin
Chen Yongxiong
Xu Binshi
ACTA METALLURGICA SINICA, 2012, 48 (03) : 289 - 297
[13] Study on crystallization of nanocrystalline/amorphous Al-based alloy
Zhang, Y. H.
Liu, Y. C.
Gao, Z. M.
Wang, D. J.
JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 469 (1-2) : 565 - 570
[14] Thermal behaviors of Al-based amorphous alloys bearing nanocrystalline In particles
Mu, J.
Zhu, Z. W.
Zhang, H. F.
Hu, Z. Q.
Wang, Y. D.
Ren, Y.
ACTA MATERIALIA, 2010, 58 (19) : 6267 - 6275
[15] OPTIMIZATION OF Al-BASED AMORPHOUS COATINGS BY WARM SPRAYING BASED ON A NUMERICAL SIMULATION AND A RESPONSE-SURFACE METHODOLOGY
Wang, Deming
Li, Tingting
Wu, Nianchu
MATERIALI IN TEHNOLOGIJE, 2024, 58 (06): : 819 - 832
[16] Preparation of Al-based Amorphous/Nanocrystalline Composite Coating on Mg-based Alloys Precipitated by Arc Spraying Process
Zhang ZhibinLiang XiubingXu Binshi State Key Laboratory for RemanufacturingAcademy of Armored Forces EngineeringBeijing China Beijing University of TechnologyBeijing China
稀有金属材料与工程, 2012, 41(S1) (S1) : 439 - 442
[17] Preparation of Al-based Amorphous/Nanocrystalline Composite Coating on Mg-based Alloys Precipitated by Arc Spraying Process
Zhang Zhibin
Liang Xiubing
Xu Binshi
RARE METAL MATERIALS AND ENGINEERING, 2012, 41 : 439 - 442
[18] On nanovoids formation in shear bands of an amorphous Al-based alloy
Aronin, A. S.
Louzguine-Luzgin, D. V.
MECHANICS OF MATERIALS, 2017, 113 : 19 - 23
[19] Cryogenic rejuvenation of Al-based amorphous-nanocrystalline alloys
Abrosimova, G.
Volkov, N.
Tran Van Tuan
Pershina, E.
Aronin, A.
MATERIALS LETTERS, 2019, 240 : 150 - 152
[20] Development and Characterization of Al-Based Amorphous Coating
Cheng, Jiangbo
Feng, Yuan
Yan, Chen
Hu, Xianlong
Li, Ruifeng
Liang, Xiubing
JOM, 2020, 72 (02) : 745 - 753

← 1 2 3 4 5 →