High temperature oxidation of Ti-46Al-6Nb-0.5W-0.5Cr-0.3Si-0.1C alloy

被引：35
作者：
Park, Soon Yong [1 ]
Seo, D. Y. [2 ]
Kim, Seong Woong [3 ]
Kim, Seung Eon [3 ]
Hong, Jae Keun [3 ]
Lee, Dong Bok [1 ]
机构：
[1] Sungkyunkwan Univ, Sch Adv Mat Sci & Engn, Suwon 16419, South Korea
[2] Natl Res Council Canada, Gas Turbine Mat Grp, Struct Mat & Mfg Lab, Aerosp Portfolio, Ottawa, ON K1A 0R6, Canada
[3] Korea Inst Mat Sci, Titanium Alloys Dept, Chang Won 51508, South Korea
来源：
INTERMETALLICS | 2016年 / 74卷
关键词：
Intermetallics (aluminides); Oxidation; Casting; Microstructure; Microscopy; various; Aerospace structures; TIAL ALLOYS; PHASE-TRANSFORMATIONS; HIGH-NB; BEHAVIOR; CR; INTERMETALLICS; RESISTANCE; NIOBIUM; AIR; SI;
D O I：
10.1016/j.intermet.2016.04.005
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
A newly developed Ti-46Al-6Nb-0.5W-0.5Cr-0.3Si-0.1C alloy was oxidized isothermally and cyclically in air, and its high-temperature oxidation behavior was investigated. When the alloy was isothermally oxidized at 700 degrees C for 2000 h, the weight gain was only 0.15 mg/cm(2). The parabolic rate constant, k(p) (mg(2)/cm(4).h), measured from isothermal oxidation tests was 0.002 at 900 degrees C and 0.009 at 1000 degrees C. Such excellent isothermal oxidation resistance resulted from the formation of the dense, continuous Al2O3 layer between the outer TiO2 layer and the inner (TiO2-rich, Al2O3-deficient) layer. The alloy also displayed good cyclic oxidation resistance at 900 degrees C. Some noticeable scale spallation began to occur after 68 h at 1000 degrees C during the cyclic oxidation test. (C) 2016 Elsevier Ltd. All rights reserved.
引用
收藏
页码：8 / 14
页数：7
相关论文
共 50 条
[41]   Oxidation resistance and micromechanical properties of a Ti-46Al-8Nb (at.%) alloy with Cr-Si magnetron-sputtered coatings [J].
Mitoraj-Krolikowska, Marzena ;
Godlewska, Elzbieta .
SURFACE & COATINGS TECHNOLOGY, 2018, 350 :732-739
[42]   High temperature oxidation of (Ti0.5Hf0.5)C ceramics fabricated by hot-pressing [J].
Shimada, S ;
Hayashi, S ;
Yunazar, F .
JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 2002, 110 (03) :167-172
[43]   High temperature tribological behavior of a Ti-46Al-2Cr-2Nb intermetallics [J].
Cheng, Jun ;
Yang, Jun ;
Zhang, Xinghua ;
Zhong, Hong ;
Ma, Jiqiang ;
Li, Fei ;
Fu, Licai ;
Bi, Qinling ;
Li, Jinshan ;
Liu, Weimin .
INTERMETALLICS, 2012, 31 :120-126
[44]   The oxidation behavior of high Cr and Al containing Nb-Si-Ti-Hf-Al-Cr alloys at 1200 and 1250 °C [J].
Su, Linfen ;
Jia, Lina ;
Jiang, Kaiyong ;
Zhang, Hu .
INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2017, 69 :131-137
[45]   The Behavior of Al0.5CoCrFeNiCuPt0.3 High-Entropy Alloy During High-Temperature Oxidation [J].
Samoilova, Olga ;
Suleymanova, Ilsiya ;
Shaburova, Nataliya ;
Moghaddam, Ahmad Ostovari ;
Trofimov, Evgeny .
HIGH TEMPERATURE CORROSION OF MATERIALS, 2024, 101 (04) :811-825
[46]   High-temperature fatigue property of Ti46Al8Nb alloy with the fully lamellar microstructure [J].
Zhou, Y. ;
Wang, J. Q. ;
Zhang, B. ;
Ke, W. ;
Han, E. H. .
INTERMETALLICS, 2012, 24 :7-14
[47]   Microstructure and high temperature oxidation behavior of Ti-Al-Nb-Si coatings on Ti-6Al-4V alloy [J].
Dai, Jingjie ;
Zhang, Nianlong ;
Wang, Amin ;
Zhang, Hongxia ;
Chen, Chuanzhong .
JOURNAL OF ALLOYS AND COMPOUNDS, 2018, 765 :46-57
[48]   The influence of the alloy microstructure on the oxidation behavior of Ti-46Al-1Cr-0.2Si alloy [J].
Pérez, P ;
Jiménez, JA ;
Frommeyer, G ;
Adeva, P .
OXIDATION OF METALS, 2000, 53 (1-2) :99-124
[49]   Effect of silicon on the kinetics and mechanisms of cyclic oxidation of titanium aluminide (Ti45Al5Nb0.5Si) developed by laser direct energy deposition [J].
Dutta, Anupama ;
Weisheit, Andreas ;
Majumdar, Jyotsna Dutta .
CORROSION SCIENCE, 2024, 231
[50]   Formation of ceramic particles in intermetallic Ti-46Al-2W-0.5Si alloy during directional solidification [J].
Lapin, J ;
Ondrús, L .
KOVOVE MATERIALY-METALLIC MATERIALS, 2002, 40 (03) :161-170
12345