Corrosion inhibition of N80 steel in hydrochloric acid by phenol derivatives

被引:0
|
作者
Vishwanatham, S. [1 ]
Haldar, Nilesh [1 ]
机构
[1] Indian Sch Mines, Dept Appl Chem, Dhanbad 826004, Bihar, India
关键词
steel; phenol; corrosion inhibition;
D O I
暂无
中图分类号
O69 [应用化学];
学科分类号
081704 ;
摘要
The inhibitory action of methoxy phenol (MPH) and nonyl phenol (NPH) on corrosion of N80 steel in 15% HCl has been investigated at different period of exposure (6 to 24 h) and temperature (30 to 110 degrees C). Nonyl phenol and methoxy phenol have shown maximum inhibition of about 83 and 78% at 75 mM inhibitor concentration in the acid respectively after 6 11 exposure test at ambient temperature. The inhibition efficiencies of nonyl phenol and methoxy phenol are found to be about 79 and 30% respectively after 24 h exposure. Nonyl phenol has shown maximum inhibition of about 59 and 44% at 75 mM inhibitor concentration in the acid respectively at 90 and 110 degrees C respectively. The inhibition afforded by rnethoxy phenol Was found to be relatively low (about 34% at 60 degrees C). Heat of adsorption was found to be 50 KJ/mol in case of MPH, indicating formation of a protective chemisorbed film on the metal surface, which Suppresses the dissolution reaction. NPH showed heat of adsorption of about 26 KJ/mol indicating a weak chemisorption. Both these compounds inhibit corrosion by adsorption mechanism and follow Temkin isotherm. The results of polarization studies indicate that the compounds are mixed type inhibitors. The FTIR spectral analyses of the surface product suggest involvement of hydroxyl group (un protonated as well as protonated) of these inhibitor molecules in the adsorption process.
引用
收藏
页码:501 / 506
页数:6
相关论文
共 50 条
  • [41] Synergistic effect of Mannich base and sodium tungstate as corrosion inhibition for N80 steel
    Wang Yun
    Hu Jun
    Wang Tian-tian
    Zheng Mao-sheng
    CAILIAO GONGCHENG-JOURNAL OF MATERIALS ENGINEERING, 2019, 47 (02): : 122 - 128
  • [42] Corrosion inhibitive properties of some new isatin derivatives on corrosion of N80 steel in 15% HCl
    Yadav, Mahendra
    Sharma, Usha
    Yadav, Premanand
    INTERNATIONAL JOURNAL OF INDUSTRIAL CHEMISTRY, 2013, 4 (01):
  • [43] CORROSION INHIBITION OF MILD STEEL IN HYDROCHLORIC ACID SOLUTION USING FATTY ACID DERIVATIVES
    Mohd, N. K.
    Ghazali, Mariyam Jameelah
    Kian, Yeong Shoot
    Ibrahim, Nor Azowa
    Yunus, Wan Md Zin Wan
    Nor, Siti Mariam Mohd
    Idris, Zainab
    JOURNAL OF OIL PALM RESEARCH, 2017, 29 (01): : 97 - 109
  • [44] Inhibition efficiency of two bipyrazole derivatives on steel corrosion in hydrochloric acid media
    Tebbji, K.
    Aouniti, A.
    Attayibat, A.
    Hammouti, B.
    Oudda, H.
    Benkaddour, M.
    Radi, S.
    Nahle, A.
    INDIAN JOURNAL OF CHEMICAL TECHNOLOGY, 2011, 18 (03) : 244 - 253
  • [45] Corrosion inhibition effect of pyrazole derivatives on mild steel in hydrochloric acid solution
    Yadav, Mahendra
    Sinha, Rajesh Ranjan
    Sarkar, Tarun Kanti
    Tiwari, Nidhi
    JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2015, 29 (16) : 1690 - 1713
  • [46] Influence of Formazan Derivatives on Corrosion Inhibition of Mild Steel in Hydrochloric Acid Medium
    Venkatesan, P.
    Anand, B.
    Matheswaran, P.
    E-JOURNAL OF CHEMISTRY, 2009, 6 : S438 - S444
  • [47] Corrosion inhibition of mild steel in boiling hydrochloric acid by some thiazole derivatives
    Quraishi, MA
    Ahmad, S
    Venkatachari, G
    BULLETIN OF ELECTROCHEMISTRY, 2002, 18 (09): : 399 - 402
  • [48] Corrosion inhibition of some azole derivatives on carbon steel in hydrochloric acid solution
    Markhali, B. P.
    Naderi, R.
    Sayebani, M.
    Mahdavian, M.
    ANTI-CORROSION METHODS AND MATERIALS, 2014, 61 (05) : 300 - 306
  • [49] Inhibition of steel corrosion by some new triazole derivatives in boiling hydrochloric acid
    Quraishi, MA
    Ahmad, S
    Ansari, MQ
    BRITISH CORROSION JOURNAL, 1997, 32 (04): : 297 - 300
  • [50] Insights into the Corrosion Inhibition Performance of Isonicotinohydrazide Derivatives for N80 Steel in 15% HCl Medium: An Experimental and Molecular Level Characterization
    Mansour, Abdelkarim Ait
    El-Haitout, Badr
    Adnin, Raihana Jannat
    Lgaz, Hassane
    Salghi, Rachid
    Lee, Han-seung
    Alhadeethi, Mustafa R.
    Messali, Mouslim
    Haboubi, Khadija
    Ali, Ismat H.
    METALS, 2023, 13 (04)