Corrosion inhibition of N80 steel in hydrochloric acid by phenol derivatives

被引:0
|
作者
Vishwanatham, S. [1 ]
Haldar, Nilesh [1 ]
机构
[1] Indian Sch Mines, Dept Appl Chem, Dhanbad 826004, Bihar, India
关键词
steel; phenol; corrosion inhibition;
D O I
暂无
中图分类号
O69 [应用化学];
学科分类号
081704 ;
摘要
The inhibitory action of methoxy phenol (MPH) and nonyl phenol (NPH) on corrosion of N80 steel in 15% HCl has been investigated at different period of exposure (6 to 24 h) and temperature (30 to 110 degrees C). Nonyl phenol and methoxy phenol have shown maximum inhibition of about 83 and 78% at 75 mM inhibitor concentration in the acid respectively after 6 11 exposure test at ambient temperature. The inhibition efficiencies of nonyl phenol and methoxy phenol are found to be about 79 and 30% respectively after 24 h exposure. Nonyl phenol has shown maximum inhibition of about 59 and 44% at 75 mM inhibitor concentration in the acid respectively at 90 and 110 degrees C respectively. The inhibition afforded by rnethoxy phenol Was found to be relatively low (about 34% at 60 degrees C). Heat of adsorption was found to be 50 KJ/mol in case of MPH, indicating formation of a protective chemisorbed film on the metal surface, which Suppresses the dissolution reaction. NPH showed heat of adsorption of about 26 KJ/mol indicating a weak chemisorption. Both these compounds inhibit corrosion by adsorption mechanism and follow Temkin isotherm. The results of polarization studies indicate that the compounds are mixed type inhibitors. The FTIR spectral analyses of the surface product suggest involvement of hydroxyl group (un protonated as well as protonated) of these inhibitor molecules in the adsorption process.
引用
收藏
页码:501 / 506
页数:6
相关论文
共 50 条
  • [31] Corrosion inhibition of N80 steel in 15% HCl by pyrazolone derivatives: electrochemical, surface and quantum chemical studies
    Ansari, K. R.
    Quraishi, M. A.
    Singh, Ambrish
    Ramkumar, Sowmya
    Obote, Ime B.
    RSC ADVANCES, 2016, 6 (29): : 24130 - 24141
  • [32] Corrosion inhibition of steel in hydrochloric acid solution by new bipyrazole derivatives
    Bouklah, M
    Hammouti, B
    Benkaddour, M
    Attayibat, A
    Radi, S
    PIGMENT & RESIN TECHNOLOGY, 2005, 34 (04) : 197 - 202
  • [33] Inhibition Effect of Pyrimidine Derivatives on the Corrosion of Steel in Hydrochloric Acid Solution
    Li Xiang-Hong
    Xie Xiao-Guang
    ACTA PHYSICO-CHIMICA SINICA, 2013, 29 (10) : 2221 - 2231
  • [34] Adsorption and corrosion inhibitive properties of synthesized hydrazine compounds on N80 steel/hydrochloric acid interface: Electrochemical and DRF studies
    Yadav, M.
    Sharma, Dipti
    Sarkar, T. K.
    JOURNAL OF MOLECULAR LIQUIDS, 2015, 212 : 451 - 460
  • [35] THE INHIBITORY EFFECT OF SOME BIPYRIDINE DERIVATIVES ON THE CORROSION BEHAVIOR OF N80 CARBON STEEL IN SULPHURIC ACID SOLUTIONS
    Liu, Xia
    Okafor, Peter C.
    Jiang, Bin
    Hu, Hongxiang
    Zheng, Yugui
    SURFACE REVIEW AND LETTERS, 2015, 22 (01)
  • [36] Optimization and evaluation of corrosion inhibitors for N80 steel in sulfamic acid solutions
    Luo, Xiyi
    Li, Ce
    Liu, Pingli
    Fu, Yangyang
    Du, Juan
    Chen, Xiang
    Liu, Jinming
    Zuo, Zixuan
    Zhao, Liangbo
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2024, 19 (10):
  • [37] Experimental and Quantum Chemical Studies on Corrosion Inhibition Effect of Synthesized Organic Compounds on N80 Steel in Hydrochloric Acid (vol 52, pg 14019, 2013)
    Kumar, Sumit
    Sharma, Dipti
    Yadav, Premanand
    Yadav, Mahendra
    INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH, 2018, 57 (31) : 10718 - 10718
  • [38] Corrosion inhibition of N-80 steel and mild steel in 15% boiling hydrochloric acid by a triazole compound - SAHMT
    Quraishi, MA
    Jamal, D
    MATERIALS CHEMISTRY AND PHYSICS, 2001, 68 (1-3) : 283 - 287
  • [39] Ultrasound-assisted synthesis of substituted triazines and their corrosion inhibition behavior on N80 steel/acid interface
    Salman, Mohammad
    Ansari, Kashif R.
    Haque, Jiyaul
    Srivastava, Vandana
    Quraishi, Mumtaz A.
    Mazumder, Mohammad A. J.
    JOURNAL OF HETEROCYCLIC CHEMISTRY, 2020, 57 (05) : 2157 - 2172
  • [40] Evaluation of Carbon Dioxide Corrosion on N80 Steel
    Fan, Zhenzhong
    Tong, Anqi
    Cui, Yan
    Yang, Junfeng
    MECHANICAL DESIGN AND POWER ENGINEERING, PTS 1 AND 2, 2014, 490-491 : 311 - +