Effect of MAF-6 Crystal Size on Its Physicochemical and Catalytic Properties in the Cycloaddition of CO2 to Propylene Oxide

Zeolitic imidazolate frameworks MAF-5 and MAF-6 based on Zn2+ and 2-ethylimidazole were demonstrated to be efficient heterogeneous catalysts in solvent-free coupling of CO2 and propylene oxide (PO) to produce propylene carbonate (PC) at 0.8 MPa of CO2 and 80 degrees C. Activity of MAF-5 was lower in comparison with MAF-6 due to the difference in their structural and textural characteristics. MAF-6 samples with particle size of 190 +/- 20, 360 +/- 30, and 810 +/- 30 nm were prepared at room temperature from [Zn(NH3)(4)](OH)(2) and 2-ethylimidazole. Control of particle size was achieved by variation of type of alcohol in alcohol/cyclohexane media for the preparation of MAF-6. According to this comprehensive study, the yield of PC was found to decrease with increasing crystal size of the MAF-6 material, which was related to the change in textural properties and the number and localization of active sites. The combination of MAF-6 with particle size of with particle size of 190 +/- 20 nm and tetrabutylammonium bromide ([n-Bu4N]Br) as co-catalyst led to an approximately 4-fold enhancement in the yield of PC (80.5%). Compared with reported ZIFs catalysts, the efficiencies of MAF-5/[n-Bu4N]Br and MAF-6/[n-Bu4N]Br binary systems were comparable and higher under similar reaction conditions.