Finite element analysis of oxidation induced metal depletion at oxide-metal interface

被引:15
作者
Zhou, Honggang [1 ]
Qu, Jianmin [1 ,2 ]
Cherkaoui, Mohammed [1 ,2 ]
机构
[1] Georgia Inst Technol, Sch Mech Engn, Atlanta, GA 30322 USA
[2] UMI 2958 GT CNRS, F-57000 Metz, France
关键词
Cr-Fe alloys; Oxidation; Stress; Finite element; Voronoi tessellation; SELECTIVE OXIDATION; GROWTH STRESSES; ALLOYS; MICROSTRUCTURE; GENERATION; SIMULATION; BEHAVIOR; DAMAGE; MODEL;
D O I
10.1016/j.commatsci.2010.03.044
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
In many situations, chromium depletion and voiding below oxide/alloy interface accompany with the selective oxidation of Cr-contained alloys. At the same time, stresses are induced at the oxide/alloy interface, in the metal and in the oxide. The combination of depletion and stress generation initiates interfacial crack-like voids which eventually lead to spallation of the oxide scale. In this paper, a continuum thermodynamic model which accounts for stress-diffusion interaction in the oxidation of Cr-Fe alloys is carried out via a two-dimension finite element implementation. For the purpose of generating depletion areas, grain areas and grain boundary areas in the alloy are defined via random Voronoi tessellation. Periodic boundary condition is also employed. The model predicts that the depletion of chromium mostly occurs at the fast diffusion area (grain boundary), and large normal tensile stresses are generated at both metal-scale interface and alloy grain boundaries. Once the depletion-induced voids reaches a certain level at the interface, concentration of stress could induce further propagation of interfacial crack. Published by Elsevier B.V.
引用
收藏
页码:842 / 847
页数:6
相关论文
共 22 条
[1]   The lateral growth strain accompanying the formation of a thermally grown oxide [J].
Clarke, DR .
ACTA MATERIALIA, 2003, 51 (05) :1393-1407
[2]   A theory for stress-driven interfacial damage upon cationic-selective oxidation of alloys [J].
El Kadiri, H. ;
Horstemeyer, M. F. ;
Bammann, D. J. .
JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 2008, 56 (12) :3392-3415
[3]   Periodic three-dimensional mesh generation for crystalline aggregates based on Voronoi tessellations [J].
Fritzen, Felix ;
Boehlke, Thomas ;
Schnack, Eckart .
COMPUTATIONAL MECHANICS, 2009, 43 (05) :701-713
[4]   DIFFUSION-MODEL FOR THE OXIDATION OF ZIRCONIUM AT 573-K AND 623-K [J].
GARCIA, EA ;
KOVACS, J .
JOURNAL OF NUCLEAR MATERIALS, 1994, 210 (1-2) :78-83
[5]   Young's modulus of 2D cellular structures under periodic boundary conditions and subject to structural effects [J].
Guessasma, S. .
COMPUTATIONAL MATERIALS SCIENCE, 2008, 44 (02) :552-565
[6]   OBSERVATIONS OF METAL OXIDE INTERFACE FOR A FE-CR ALLOY [J].
HOWES, VR .
CORROSION SCIENCE, 1968, 8 (04) :221-&
[7]   Simulation for intergranular stress corrosion cracking based on a three-dimensional polycrystalline model [J].
Kamaya, Masayuki ;
Itakura, Mitsuhiro .
ENGINEERING FRACTURE MECHANICS, 2009, 76 (03) :386-401
[8]   SIMULATION OF MATERIAL MICROSTRUCTURE USING A 3D VORONOI TESSELLATION - CALCULATION OF EFFECTIVE THERMAL-EXPANSION COEFFICIENT OF POLYCRYSTALLINE MATERIALS [J].
KUMAR, S ;
KURTZ, SK .
ACTA METALLURGICA ET MATERIALIA, 1994, 42 (12) :3917-3927
[9]   Oxidation behavior of Fe-16Cr alloy interconnect for SOFC under hydrogen potential gradient [J].
Kurokawa, H ;
Kawamura, K ;
Maruyama, T .
SOLID STATE IONICS, 2004, 168 (1-2) :13-21
[10]   Mechanical behaviour of alloys containing heterogeneously distributed particles:: Modelling with Delaunay triangulation [J].
Lépinoux, J ;
Estrin, Y .
ACTA MATERIALIA, 2000, 48 (17) :4337-4347