In vitro bioactivity of S520 glass fibers and initial assessment of osteoblast attachment

被引:46
作者
Clupper, DC
Gough, JE
Hall, MM
Clare, AG
LaCourse, WC
Hench, LL
机构
[1] Univ London Imperial Coll Sci Technol & Med, Ctr Tissue Engn, Dept Mat, London SW7 2BP, England
[2] Alfred Univ, Dept Ceram Engn & Mat Sci, Alfred, NY 14802 USA
来源
JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART A | 2003年 / 67A卷 / 01期
关键词
glass fibers; bioactivity; hydroxyapatite; cell attachment; mineralization;
D O I
10.1002/jbm.a.10040
中图分类号
R318 [生物医学工程];
学科分类号
0831 ;
摘要
Bioactive glass fibers are attractive materials for use as tissue-engineering scaffolds and as the reinforcing phase for resorbable bioactive composites. The bioactivity of S520 glass fibers (52.0 mol % SiO2, 20.9 Na2O, 7.1 K2O, 18.0 CaO, and 2.0 P2O5) was evaluated in two media, simulated body fluid (SBF) and Dulbecco's modified Eagle's medium (DMEM), for up to 20 days at 37degreesC. Hydroxyapatite formation was observed on S520 fiber surfaces after 5 h in SBF. After a 20-day immersion, a continuous hydroxyapatite layer was present on the surface of samples immersed in SBF as well as on those samples immersed in DMEM [fiber surface area to solution volume ratio (SAX) of 0.10 cm(2)/mL]. Backscattered electron imaging and EDS analysis revealed that the hydroxyapatite layer formation was more extensive for samples immersed in SBF. Decreasing the SAN ratio to 0.05 cm(2)/mL decreased the time required to form a continuous hydroxyapatite surface layer. ICP was used to reveal Si, Ca, and P release profiles in DMEM after the 1st h (15.1, 83.8, and 29.7 ppm, respectively) were similar to those concentrations previously determined to stimulate gene expression in osteoblasts in vitro (16.5, 83.3, and 30.4 ppm, respectively). The tensile strength of the 20-mum diameter fibers was 925 +/- 424 MPa. Primary human osteoblast attachment to the fiber surface was studied by using SEM, and mineralization was studied by using alizarin red staining. Osteoblast dorsal ruffles, cell projections, and lamellipodia were observed, and by 7 days, cells had proliferated to form monolayer areas as shown by SEM. At 14 days, nodule formation was observed, and these nodules stained positive for alizarin red, demonstrating Ca deposition and, therefore mineralization. (C) 2003 Wiley Periodicals, Inc.
引用
收藏
页码:285 / 294
页数:10
相关论文
共 37 条
[1]   Development of mineralized nodules in fetal rat mandibular osteogenic precursor cells:: Requirement for dexamethasone but not for β-glycerophosphate [J].
Abe, Y ;
Aida, Y ;
Abe, T ;
Hirofuji, T ;
Anan, H ;
Maeda, K .
CALCIFIED TISSUE INTERNATIONAL, 2000, 66 (01) :66-69
[2]   Evidence for calcium phosphate supersaturation in the loop of Henle [J].
Asplin, JR ;
Mandel, NS ;
Coe, FL .
AMERICAN JOURNAL OF PHYSIOLOGY-RENAL FLUID AND ELECTROLYTE PHYSIOLOGY, 1996, 270 (04) :F604-F613
[3]  
*ASTM, 337675 D ASTM
[4]  
Brink M, 1997, J BIOMED MATER RES, V37, P114, DOI 10.1002/(SICI)1097-4636(199710)37:1<114::AID-JBM14>3.0.CO
[5]  
2-G
[6]   SILICON - A REQUIREMENT IN BONE-FORMATION INDEPENDENT OF VITAMIN-D1 [J].
CARLISLE, EM .
CALCIFIED TISSUE INTERNATIONAL, 1981, 33 (01) :27-34
[7]  
CLAPP PI, 2001, THESIS ALFRED U
[8]   AUGER SPECTROSCOPIC ANALYSIS OF BIOGLASS CORROSION FILMS [J].
CLARK, AE ;
PANTANO, CG ;
HENCH, LL .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1976, 59 (1-2) :37-39
[9]  
Clupper DC, 2001, J BIOMED MATER RES, V57, P532, DOI 10.1002/1097-4636(20011215)57:4<532::AID-JBM1199>3.0.CO
[10]  
2-3