Insight into hydrostatic pressure effects on diffusible hydrogen content in wet welding joints using in-situ X-ray imaging method

被引:21
作者
Chen, Hao [1 ,2 ]
Guo, Ning [1 ,2 ,3 ]
Liu, Cheng [2 ]
Zhang, Xin [1 ,2 ]
Xu, Changsheng [1 ,2 ]
Wang, Guodong [1 ,2 ]
机构
[1] Harbin Inst Technol, State Key Lab Adv Welding & Joining, Harbin 150001, Peoples R China
[2] Harbin Inst Technol Weihai, Shandong Prov Key Lab Special Welding Technol, Weihai 264209, Peoples R China
[3] Shandong Inst Shipbldg Technol, Weihai 264209, Peoples R China
关键词
Underwater wet welding; Diffusible hydrogen; Hydrostatic pressure; X-ray imaging method; APPARENT DIFFUSIVITY; METAL TRANSFER; STEEL; CRACKING; EMBRITTLEMENT; STABILITY;
D O I
10.1016/j.ijhydene.2020.01.195
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
In this study, a special phenomenon of gas evolution in the metal droplet and melt pool during underwater wet welding was investigated by in-situ imaging method in a simulated deep-water environment. In general, the dissolved hydrogen escaped from molten droplet and molten pool in the form of bubbles during molten metal solidification. As the increase of hydrostatic pressure, the gas cannot expand enough to burst the droplet and release gas, but instead of entering into molten pool again. The combinations of the internal pressure in the bubble and hydrogen-rich atmosphere induced by welding arc resulted in that the melt pool has been subjected to dual influences. The diffusible hydrogen content in the deposited metal significantly increased from 23.3 to 66.3 ml/100 g with increasing the water depth to 150 m, which was related to the high hydrogen partial pressure and the rapid solidification rate of molten metal. (C) 2020 Hydrogen Energy Publications LLC. Published by Elsevier Ltd.
引用
收藏
页码:10219 / 10226
页数:8
相关论文
共 44 条
  • [1] Ando S., 1983, P INT C TRONDH NORW, P255, DOI 10.1016/B978-0-08-030537-0.50027-2
  • [2] In-situ observations of melt degassing and hydrogen removal enhanced by ultrasonics in underwater wet welding
    Chen, Hao
    Guo, Ning
    Xu, Kexin
    Xu, Changsheng
    Zhou, Li
    Wang, Guodong
    [J]. MATERIALS & DESIGN, 2020, 188
  • [3] Effects of arc bubble behaviors and characteristics on droplet transfer in underwater wet welding using in-situ imaging method
    Chen, Hao
    Guo, Ning
    Huang, Lu
    Zhang, Xin
    Feng, Jicai
    Wang, Guodong
    [J]. MATERIALS & DESIGN, 2019, 170
  • [4] Effect of hydrostatic pressure on protective bubble characteristic and weld quality in underwater flux-cored wire wet welding
    Chen, Hao
    Guo, Ning
    Shi, Xianghua
    Du, Yongpeng
    Feng, Jicai
    Wang, Guodong
    [J]. JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2018, 259 : 159 - 168
  • [5] Effect of water flow on the arc stability and metal transfer in underwater flux-cored wet welding
    Chen, Hao
    Guo, Ning
    Shi, Xianghua
    Du, Yongpeng
    Feng, Jicai
    Wang, Guodong
    [J]. JOURNAL OF MANUFACTURING PROCESSES, 2018, 31 : 103 - 115
  • [6] Effect of Water Depth on Diffusible Hydrogen on Wet Welds
    Dias da Silva, Weslley Carlos
    Bracarense, Alexandre Queiroz
    Pereira Pessoa, Ezequiel Caires
    [J]. SOLDAGEM & INSPECAO, 2012, 17 (04): : 298 - 305
  • [7] Reducing diffusible hydrogen contents of shielded metal arc welds through addition of flux-oxidizing ingredients
    duPlessis, J.
    duToit, M.
    [J]. JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2008, 17 (01) : 50 - 56
  • [8] Investigation on dynamic behaviors of bubble evolution in underwater wet flux-cored arc welding
    Feng, Jicai
    Wang, Jianfeng
    Sun, Qingjie
    Zhao, Huanyao
    Wu, Laijun
    Xu, Pengwei
    [J]. JOURNAL OF MANUFACTURING PROCESSES, 2017, 28 : 156 - 167
  • [9] Fydrych D, 2015, METALL ITAL, P47
  • [10] An experimental study of high-hydrogen welding processes
    Fydrych, Dariusz
    Labanowski, Jerzy
    [J]. REVISTA DE METALURGIA, 2015, 51 (04)