Annealing temperature dependent ZnCo2O4 nanosheet arrays supported on Ni foam for high-performance asymmetric supercapacitor

被引:40
作者
Li, Xizi [1 ]
Zhang, Mingyi [1 ]
Wu, Lili [1 ,2 ]
Fu, Qishan [1 ]
Gao, Hong [1 ]
机构
[1] Harbin Normal Univ, Key Lab Photon & Elect Bandgap Mat, Minist Educ, Sch Phys & Elect Engn, Harbin 150025, Heilongjiang, Peoples R China
[2] Heilongjiang Univ Sci & Technol, Ctr Engn Training & Basic Expt, Harbin 150022, Heilongjiang, Peoples R China
基金
中国国家自然科学基金;
关键词
ZnCo2O4; Nanosheets; Annealing; Asymmetric supercapacitor; NICKEL FOAM; SUPERIOR PERFORMANCE; FACILE SYNTHESIS; NANOFLAKE ARRAY; NANOWIRE ARRAYS; ENERGY-STORAGE; CARBON CLOTH; THIN SHEETS; ELECTRODES; NANOPARTICLES;
D O I
10.1016/j.jallcom.2018.09.197
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Porous network ZnCo2O4 nanosheets are successfully achieved by a simple hydrothermal process and adjusting the annealing temperature. The electrochemical performance of ZnCo2O4 nanosheets is significantly influenced by different annealing temperatures. It has been discovered that electrode of ZnCo2O4 that has be annealed at 200 degrees C shows an ultrahigh areal capacitance of 3.19 F cm(-2) at a current density of 2 mA cm(-2). An asymmetric supercapacitor device was assembled by ZnCo2O4 annealed at 200 degrees C as positive electrode and activated carbon as negative electrode, which exhibits the energy densities of 50.7 and 37.7 Wh kg(-1) at power densities of 187.6 and 2950.4 W kg(-1), respectively. (C) 2018 Elsevier B.V. All rights reserved.
引用
收藏
页码:367 / 375
页数:9
相关论文
共 50 条
[1]   INNER AND OUTER ACTIVE SURFACE OF RUO2 ELECTRODES [J].
ARDIZZONE, S ;
FREGONARA, G ;
TRASATTI, S .
ELECTROCHIMICA ACTA, 1990, 35 (01) :263-267
[2]   Preparation of ZnCo2O4 nanoflowers on a 3D carbon nanotube/nitrogen-doped graphene film and its electrochemical capacitance [J].
Bai, Wenlong ;
Tong, Hao ;
Gao, Zhenzhen ;
Yue, Shihong ;
Xing, Sichuan ;
Dong, Shengyang ;
Shen, Laifa ;
He, Jianping ;
Zhang, Xiaogang ;
Liang, Yanyu .
JOURNAL OF MATERIALS CHEMISTRY A, 2015, 3 (43) :21891-21898
[3]   Hierarchical polypyrrole based composites for high performance asymmetric supercapacitors [J].
Chen, Gao-Feng ;
Liu, Zhao-Qing ;
Lin, Jia-Ming ;
Li, Nan ;
Su, Yu-Zhi .
JOURNAL OF POWER SOURCES, 2015, 283 :484-493
[4]   Mesoporous ZnCo2O4 nanoflakes grown on nickel foam as electrodes for high performance supercapacitors [J].
Cheng, Jinbing ;
Lu, Yang ;
Qiu, Kangwen ;
Yan, Hailong ;
Hou, Xiaoyi ;
Xu, Jinyou ;
Han, Lei ;
Liu, Xianming ;
Kim, Jang-Kyo ;
Luo, Yongsong .
PHYSICAL CHEMISTRY CHEMICAL PHYSICS, 2015, 17 (26) :17016-17022
[5]   Rationally designed hierarchical ZnCo2O4/Ni(OH)2 nanostructures for high-performance pseudocapacitor electrodes [J].
Chuo, H. X. ;
Gao, H. ;
Yang, Q. ;
Zhang, N. ;
Bu, W. B. ;
Zhang, X. T. .
JOURNAL OF MATERIALS CHEMISTRY A, 2014, 2 (48) :20462-20469
[6]  
Conway B, 1999, ELECTROCHEMICAL SUPE
[7]   Crystalline NiCo2S4 nanotube array coated with amorphous NiCoxSy for supercapacitor electrodes [J].
Ding, Rui ;
Zhang, Mingyi ;
Yao, Yunhe ;
Gao, Hong .
JOURNAL OF COLLOID AND INTERFACE SCIENCE, 2016, 467 :140-147
[8]   Controllable synthesis of Ni3-xCoxS4 nanotube arrays with different aspect ratios grown on carbon cloth for high-capacity supercapacitors [J].
Ding, Rui ;
Gao, Hong ;
Zhang, MingYi ;
Zhang, Jing ;
Zhang, XiTian .
RSC ADVANCES, 2015, 5 (60) :48631-48637
[9]   Electrical Energy Storage for the Grid: A Battery of Choices [J].
Dunn, Bruce ;
Kamath, Haresh ;
Tarascon, Jean-Marie .
SCIENCE, 2011, 334 (6058) :928-935
[10]   Free-standing Ti3C2Tx electrode with ultrahigh volumetric capacitance [J].
Fu, Qishan ;
Wen, Jing ;
Zhang, Na ;
Wu, Lili ;
Zhang, Mingyi ;
Lin, Shuangyan ;
Gao, Hong ;
Zhang, Xitian .
RSC ADVANCES, 2017, 7 (20) :11998-12005