Novel PdAgCu ternary alloy: Hydrogen permeation and surface properties

Dense PdAgCu ternary alloy composite membranes were synthesized by the sequential electroless plating of Pd, Ag and Cu on top of both disk and tubular porous stainless steel substrates. X-ray diffraction and scanning electron microscopy were employed to study the structure and morphology of the tested samples. The hydrogen permeation performance of these membranes was investigated over a 350-450 degrees C temperature range and a trans-membrane pressure up to 100 kPa. After annealing at 500 degrees C in hydrogen stream followed by permeation experiments, the alloy layer presented a FCC crystalline phase with a bulk concentration of 68% Pd, 7% Ag and 25% Cu as revealed by EDS. The PdAgCu tubular membrane was found to be stable during more than 300 h on hydrogen stream. The permeabilities of the PdAgCu ternary alloy samples were higher than the permeabilities of the PdCu alloy membranes with a FCC phase. The co-segregation of silver and copper to the membrane surface was observed after hydrogen permeation experiments at high temperature as determined by XPS. (C) 2011 Elsevier B.V. All rights reserved.