Eddy current inspection of closed fatigue and stress corrosion cracks

被引：50
|
作者：
Yusa, Noritaka [2 ]
Perrin, Stephane
Mizuno, Kazue
Chen, Zhenmao
Miya, Kenzo
机构：
[1] IIU, Tokyo 1100008, Japan
[2] Univ Tokyo, Dept Nucl Engn & Management, Grad Sch Engn, Tokyo, Japan
[3] Xi An Jiao Tong Univ, MOE Key Lab Strength & Vibrat, Xian, Peoples R China
来源：
MEASUREMENT SCIENCE AND TECHNOLOGY | 2007年 / 18卷 / 11期
关键词：
electromagnetic non-destructive evaluation; fatigue crack; stress corrosion cracking; austenitic stainless steel;
D O I：
10.1088/0957-0233/18/11/021
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
This study evaluates the effect of loading on closed crack openings on eddy current signals caused by the crack. Three plate specimens having a fatigue crack and another three specimens having stress corrosion cracking are prepared. Four-point bending of the specimens is carried out to introduce compressive stress to close the opening of the cracks. Then eddy current signals due to the crack are gathered using a plus point type probe. The bending was conducted with a variable load; the eddy current signals remain almost unchanged regardless of the loading.
引用
收藏
页码：3403 / 3408
页数：6
相关论文
共 50 条
  • [21] Effect of Crack Closure on Quantitative ECT Inspection of Closed Fatigue Cracks
    Chen, Zhenmao
    Yusa, Noritaka
    Miya, Kenzo
    Tokuma, Hideaki
    ELECTROMAGNETIC NONDESTRUCTIVE EVALUATION (XI), 2008, 31 : 171 - 178
  • [22] DETECTION OF FATIGUE CRACKS IN NONMAGNETIC MATERIALS BY THE EDDY CURRENT METHOD
    DANILOV, YS
    RUBLEV, YA
    INDUSTRIAL LABORATORY, 1962, 28 (11): : 1427 - 1429
  • [23] EDDY-CURRENT FLAW DETECTOR FOR REVEALING FATIGUE CRACKS
    ZELTSER, VS
    KUZMITSKII, ML
    SOVIET JOURNAL OF NONDESTRUCTIVE TESTING-USSR, 1978, 14 (07): : 662 - 663
  • [24] Pulsed eddy current for metal surface cracks inspection: Theory and experiment
    Tai, CC
    Yang, HC
    Liang, DS
    REVIEW OF PROGRESS IN QUANTITATIVE NONDESTRUCTIVE EVALUATION, VOLS 21A & B, 2002, 615 : 388 - 395
  • [25] PULSED EDDY-CURRENT INSPECTION OF CRACKS UNDER INSTALLED FASTENERS
    GIBBS, M
    CAMPBELL, J
    MATERIALS EVALUATION, 1991, 49 (01) : 51 - &
  • [26] Quantification of closed cracks in railways using eddy current pulsed thermography
    Yin, Hui
    Peng, Jianping
    Zhang, Xiang
    Tian, Kang
    Zhang, Yu
    Guo, Jianqiang
    APPLIED OPTICS, 2021, 60 (17) : 5195 - 5202
  • [27] The Study of Possibility of Stress-Corrosion Cracks Group Resolution by Eddy-Current Flaw Detector
    Moskovkina, V.N.
    Zagidulin, R.V.
    IOP Conference Series: Earth and Environmental Science, 2020, 459 (04)
  • [28] Chemical and electrochemical conditions within stress corrosion and corrosion fatigue cracks
    Leslie G. Bland
    Jenifer S. (Warner) Locke
    npj Materials Degradation, 1
  • [29] Chemical and electrochemical conditions within stress corrosion and corrosion fatigue cracks
    Bland, Leslie G.
    Locke, Jenifer S.
    NPJ MATERIALS DEGRADATION, 2017, 1 (01)
  • [30] Multifrequency eddy current inspection of corrosion in clad aluminum riveted lap joints and its effect on fatigue life
    Okafor, A. C.
    Natarajan, S.
    REVIEW OF PROGRESS IN QUANTITATIVE NONDESTRUCTIVE EVALUATION, VOLS 26A AND 26B, 2007, 894 : 1274 - +
12345