Eddy current inspection of closed fatigue and stress corrosion cracks

被引：50
|
作者：
Yusa, Noritaka [2 ]
Perrin, Stephane
Mizuno, Kazue
Chen, Zhenmao
Miya, Kenzo
机构：
[1] IIU, Tokyo 1100008, Japan
[2] Univ Tokyo, Dept Nucl Engn & Management, Grad Sch Engn, Tokyo, Japan
[3] Xi An Jiao Tong Univ, MOE Key Lab Strength & Vibrat, Xian, Peoples R China
来源：
MEASUREMENT SCIENCE AND TECHNOLOGY | 2007年 / 18卷 / 11期
关键词：
electromagnetic non-destructive evaluation; fatigue crack; stress corrosion cracking; austenitic stainless steel;
D O I：
10.1088/0957-0233/18/11/021
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
This study evaluates the effect of loading on closed crack openings on eddy current signals caused by the crack. Three plate specimens having a fatigue crack and another three specimens having stress corrosion cracking are prepared. Four-point bending of the specimens is carried out to introduce compressive stress to close the opening of the cracks. Then eddy current signals due to the crack are gathered using a plus point type probe. The bending was conducted with a variable load; the eddy current signals remain almost unchanged regardless of the loading.
引用
收藏
页码：3403 / 3408
页数：6
相关论文
共 50 条
  • [1] Automatic discrimination of stress corrosion and fatigue cracks using eddy current testing
    Perrin, Stéphane
    Yusa, Noritaka
    Miya, Kenzo
    Studies in Applied Electromagnetics and Mechanics, 2007, 28 : 91 - 98
  • [2] MAPPING STRESS CORROSION CRACKS USING EDDY CURRENT ARRAY SENSORS
    Tomar, Munendra S.
    Fingerhut, Martin
    Hansen, Ben
    IPC2008: PROCEEDINGS OF THE ASME INTERNATIONAL PIPELINE CONFERENCE - 2008, VOL 2, 2009, : 705 - 711
  • [3] A nondestructive strategy for the distinction of natural fatigue and stress corrosion cracks based on signals from eddy current testing
    Chen, Zhenmao
    Janousek, Ladislav
    Yusa, Noritaka
    Miya, Kenzo
    JOURNAL OF PRESSURE VESSEL TECHNOLOGY-TRANSACTIONS OF THE ASME, 2007, 129 (04): : 719 - 728
  • [4] Eddy current inspection for intergranular corrosion
    Mook, G
    Göllner, J
    Köser, O
    Mook, B
    Schultze, S
    MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK, 2003, 34 (02) : 225 - 231
  • [5] Discussion on the equivalent conductivity and resistance of stress corrosion cracks in eddy current simulations
    Yusa, Noritaka
    Miya, Kenzo
    NDT & E INTERNATIONAL, 2009, 42 (01) : 9 - 15
  • [6] A numerical study on eddy current signal characteristics of imitative stress corrosion cracks
    Jomdecha, Cherdpong
    Cai, Wenlu
    Xie, Shejuan
    Chen, Zhenmao
    Li, Peng
    INTERNATIONAL JOURNAL OF APPLIED ELECTROMAGNETICS AND MECHANICS, 2017, 55 (02) : 257 - 269
  • [7] Reconstruction of stress corrosion cracks using signals of pulsed eddy current testing
    Wang, Li
    Xie, Shejuan
    Chen, Zhenmao
    Li, Yong
    Wang, Xiaowei
    Takagi, Toshiyuki
    NONDESTRUCTIVE TESTING AND EVALUATION, 2013, 28 (02) : 145 - 154
  • [8] EDDY-CURRENT INSPECTION OF CRACKS IN A MULTILAYER CONDUCTOR
    BURKE, SK
    JOURNAL OF APPLIED PHYSICS, 1990, 67 (01) : 465 - 476
  • [9] Eddy-current inspection system avoids cracks
    Kopka, Thomas
    Schwer, Anton
    Wire, 2002, 52 (02): : 100 - 102
  • [10] Magneto-optic/eddy current imaging of subsurface corrosion and fatigue cracks in aging aircraft
    Fitzpatrick, GL
    Thome, DK
    Skaugset, RL
    Shih, WCL
    REVIEW OF PROGRESS IN QUANTITATIVE NONDESTRUCTIVE EVALUATION, VOLS 15A AND 15B, 1996, 15 : 1159 - 1166
12345