Recycling of wood fiber-reinforced HDPE by multiple reprocessing

被引:15
作者
Akesson, Dan [1 ]
Fuchs, Torsten [1 ]
Stoss, Michael [1 ]
Root, Andrew [2 ]
Stenvall, Erik [3 ]
Skrifvars, Mikael [1 ]
机构
[1] Univ Boras, Swedish Ctr Resource Recovery, Boras, Sweden
[2] MagSol, Tuhkanummenkuja 2, Helsinki 00970, Finland
[3] Chalmers, Dept Mat & Mfg Technol, Gothenburg, Sweden
关键词
biopolymers and renewable polymers; cellulose and other wood products; composites; polyolefins; recycling; HIGH-DENSITY POLYETHYLENE; MECHANICAL-PROPERTIES; PLASTIC COMPOSITES; POLYPROPYLENE COMPOSITES; DEGRADATION; BEHAVIOR; FLOUR;
D O I
10.1002/app.43877
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
The mechanical recycling of high-density polyethylene (HDPE) reinforced with wood fiber was studied by means of repeated injection moulding. The change in properties during the recycling was monitored by tensile and flexural tests, Charpy impact tests, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), FTIR spectroscopy, and by measuring the fiber lengths. Tests were also done where injection moulding was combined with subsequent accelerated thermo-oxidative ageing and thereafter repeated numerous times. The results showed that the HDPE composites were relatively stable toward both the ageing conditions and the repeated injection moulding. The change of the mechanical properties was mainly observed as an increased elongation at max. (C) 2016 Wiley Periodicals, Inc.
引用
收藏
页数:8
相关论文
共 33 条
[1]   Effects of a mixture of stabilizers on the structure and mechanical properties of polyethylene during reprocessing [J].
Abad, MJ ;
Ares, A ;
Barral, L ;
Cano, J ;
Díez, FJ ;
García-Garabal, S ;
López, J ;
Ramírez, C .
JOURNAL OF APPLIED POLYMER SCIENCE, 2004, 92 (06) :3910-3916
[2]   Dimensional stability and mechanical behaviour of wood-plastic composites based on recycled and virgin high-density polyethylene (HDPE) [J].
Adhikary, Kamal B. ;
Pang, Shusheng ;
Staiger, Mark P. .
COMPOSITES PART B-ENGINEERING, 2008, 39 (05) :807-815
[3]   THERMODYNAMIC PROPERTIES OF IDEALLY CRYSTALLINE POLYETHYLENE [J].
ATKINSON, CM ;
RICHARDS.MJ .
TRANSACTIONS OF THE FARADAY SOCIETY, 1969, 65 (559P) :1764-+
[4]   Recycling effect on mechanical behavior of HDPE/glass fibers at low concentrations [J].
Ayadi, A. ;
Kraiem, D. ;
Bradai, C. ;
Pimbert, S. .
JOURNAL OF THERMOPLASTIC COMPOSITE MATERIALS, 2012, 25 (05) :523-536
[5]   The effect of reprocessing on the mechanical properties of the waste fabric reinforced composites [J].
Bakkal, Mustafa ;
Bodur, Mehmet S. ;
Berkalp, Omer B. ;
Yilmaz, Safak .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2012, 212 (11) :2541-2548
[6]   Reprocessing of wood fibre reinforced polypropylene composites. Part I: Effects on physical and mechanical properties [J].
Beg, M. D. H. ;
Pickering, K. L. .
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2008, 39 (07) :1091-1100
[7]   Simulated recycling of post-consumer high density polyethylene material [J].
Boldizar, A ;
Jansson, A ;
Gevert, T ;
Möller, K .
POLYMER DEGRADATION AND STABILITY, 2000, 68 (03) :317-319
[8]   Degradation of ABS during repeated processing and accelerated ageing [J].
Boldizar, A ;
Möller, K .
POLYMER DEGRADATION AND STABILITY, 2003, 81 (02) :359-366
[9]   Investigations on the recycling of hemp and sisal fibre reinforced polypropylene composites [J].
Bourmaud, A. ;
Baley, C. .
POLYMER DEGRADATION AND STABILITY, 2007, 92 (06) :1034-1045
[10]   Accelerated aging and lifetime prediction: Review of non-Arrhenius behaviour due to two competing processes [J].
Celina, M ;
Gillen, KT ;
Assink, RA .
POLYMER DEGRADATION AND STABILITY, 2005, 90 (03) :395-404