High-temperature oxidation behavior of NiCrA1Y bond coats and Stellite-6 plasma-sprayed coatings

被引：38

作者：

Sidhu, BS ^{[1
]}

Prakash, S

机构：

[1] GZS, Coll Engn & Technol, Mech Engn Dept, Bathinda 151001, India

[2] Indian Inst Technol, Met & Mat Engn Dept, Roorkee 247667, Uttar Pradesh, India

来源：

OXIDATION OF METALS | 2005年 / 63卷 / 3-4期

关键词：

coatings; plasma spray; NiCrA1Y; Stellite-6; oxidation;

D O I：

10.1007/s11085-005-3203-1

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

Ni-22Cr-10Al-1Y and Stellite-6 coatings were deposited on boiler-tube steels, namely ASTM-SA210-Grade A1, ASTM- SA213-T-11 and ASTM-SA213-T- 22, by a shrouded plasma-spray process. The NiCrAlY alloy powder was also sprayed as a bond coat before applying a Stellite-6 coating. The cyclic-oxidation behavior of the NiCrAlY bond coats and Stellite-6 coating were evaluated at 900 degrees C. Visual observations and gravimetric data were measured at the end of each cycle. Finally, the scale was analyzed using X-ray Diffraction, Scanning-Electron Microscope, Energy-Dispersive X-Ray Studies and Electron-Probe Micro-Analyzer techniques. The coatings were found to be effective in increasing resistance to oxidation at the test temperature of 900 degrees C. The protection is higher in the case of the Stellite-6 coating. The protection is lesser for both coating types when T22 steel was the substrate and higher in the case of GrA1 steel. The deleterious behavior of Mo present in the T22 steel is perhaps responsible for conferring lesser protection.

引用

页码：241 / 259

页数：19

共 27 条

[1]

ANANTHAPADMANAB.PV, 1991, SURFACE COATINGS TEC, V49, P626

[2]

[Anonymous], 1994, 1994 THERM SPRAY

[3] High temperature oxidation of HFPD thermal-sprayed MCrAlY coatings [J].

Belzunce, FJ ;

Higuera, V ;

Poveda, S .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 297 (1-2) :162-167

[4]

BORNSTEIN NS, 1975, P C GAS TURB MAT MAR, P115

[5]

BUNSHAH RF, 2001, HDB HARD COATINGS DE

[6]

Chatterjee UK., 2001, ENV DEGRADATION META, DOI DOI 10.1201/9781482292244

[7] Abrasive wear resistance of plasma-sprayed tungsten carbide cobalt coatings [J].

Chen, H ;

Hutchings, IM .

SURFACE & COATINGS TECHNOLOGY, 1998, 107 (2-3) :106-114

[8] Cohesion in plasma-sprayed coatings - A comparison between evaluation methods [J].

Erickson, LC ;

Westergard, R ;

Wiklund, U ;

Axen, N ;

Hawthorne, HM ;

Hogmark, S .

WEAR, 1998, 214 (01) :30-37

[9] Diffusion cells and chemical failure of MCrAlY bond coats in thermal-barrier coating systems [J].

Evans, HE ;

Taylor, MP .

OXIDATION OF METALS, 2001, 55 (1-2) :17-34

[10] Transient phenomena in plasma torches and in plasma sprayed coating generation [J].

Fauchais, P ;

Coudert, JF ;

Vardelle, M .

JOURNAL DE PHYSIQUE IV, 1997, 7 (C4) :187-198

← 1 2 3 →