Effects of Thermal exposure on Microstructure and Mechanical Properties of Ni based Superalloy GTD111

被引：3

作者：

Lee, Han-sang ^{[1
]}

Yoo, Keun-bong ^{[1
]}

Kim, Doo-soo ^{[1
]}

Kim, Jae-hoon ^{[2
]}

机构：

[1] KEPCO Res Inst, Power Generat Lab, 65 Munji Ro, Taejon 305760, South Korea

[2] Chungnam Natl Univ, Dept Engn Mech, Yuseong Gu, Taejon 305764, South Korea

来源：

STRUCTURAL INTEGRITY AND FAILURE | 2011年 / 275卷

关键词：

gas turbine; thermal exposure; stress-rupture test; mechanical property; GTD111;

D O I：

10.4028/www.scientific.net/AMR.275.31

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

The rotating components in the hot sections of land-based gas turbine are exposed to severe environment during several ten thousand hours at above 1100 degrees C operating temperature. The failure mechanism of the hot gas components would be accompanied by material degradation in the properties of high temperature and creep rupture strength. Many hot gas components in gas turbine are made of Ni-based superalloy because of their high temperature performance. In this work, we surveyed the time and temperature dependent degradation of Ni-based superalloy. We prepared the specimens from GTD111 that are exposed at 871 degrees C and 982 degrees C in 1,000 similar to 10,000 hours. We carried out the mechanical test and microstructural observation.

引用

页码：31 / +

页数：2

共 50 条

[41] Influence of thermal exposure on the microstructural evolution and mechanical properties of a wrought Ni-base superalloy
Kim, I. S.
Choi, B. G.
Hong, H. U.
Do, J.
Jo, C. Y.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 593 : 55 - 63
[42] Re-heat rejuvenation study of directionally solidified GTD111 DS superalloy in service damaged gas turbine blades
Tang W.
Xiao J.
Zhang J.
Li Y.
Huazhong Keji Daxue Xuebao (Ziran Kexue Ban)/Journal of Huazhong University of Science and Technology (Natural Science Edition), 2019, 47 (03): : 76 - 81
[43] Rejuvenation Heat Treatment of Nickel Base Superalloy Grade GTD111 after Longterm Service via Taguchi Method for Optimization
Toocharoen, S.
Kaewkuekool, S.
Peasura, P.
INTERNATIONAL JOURNAL OF ENGINEERING, 2021, 34 (04): : 956 - 965
[44] The microstructure evolution and its effect on the mechanical properties of a hot-corrosion resistant Ni-based superalloy during long-term thermal exposure
Wang, Jian
Zhou, Lanzhang
Sheng, Liyuan
Guo, Jianting
MATERIALS & DESIGN, 2012, 39 : 55 - 62
[45] Long-term thermal exposure responses of the microstructure and properties of a cast Ni-base superalloy
Qin, X. Z.
Guo, J. T.
Yuan, C.
Hou, J. S.
Zhou, L. Z.
Ye, H. Q.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 543 : 121 - 128
[46] Microstructural Stability and Mechanical Properties of a Novel Weldable Ni-based Superalloy during Thermal Exposure at 800 °C
Gao, Lei
Song, Chaoqian
Zhu, Hao
Zheng, Boyuan
Liu, Xuli
Wu, Yidong
Hui, Xidong
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2025,
[47] Evolution of solidification and microstructure in laser-clad IN625 superalloy powder on GTD-111 superalloy
Cao, Yan
Farouk, Naeim
Taheri, Morteza
Yumashev, Alexei Valerievich
Bozorg, Seyed Farshid Kashani
Ojo, Olatunji Oladimeji
SURFACE & COATINGS TECHNOLOGY, 2021, 412
[48] The effect of thermal exposure on the properties of a Ni-base superalloy
Aghaie-Khafri, M.
Hajjavady, M.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 487 (1-2): : 388 - 393
[49] Microstructure development during transient liquid phase bonding of GTD-111 nickel-based superalloy
Pouranvari, M.
Ekrami, A.
Kokabi, A. H.
JOURNAL OF ALLOYS AND COMPOUNDS, 2008, 461 (1-2) : 641 - 647
[50] An investigation on the coarsening behavior of γ′ precipitate in GTD-111 Ni-base superalloy
Berahmand, Mohammad
Sajjadi, S. A.
PHASE TRANSITIONS, 2012, 85 (1-2) : 1 - 12

← 1 2 3 4 5 →