Effects of Thermal exposure on Microstructure and Mechanical Properties of Ni based Superalloy GTD111

被引：3

作者：

Lee, Han-sang ^{[1
]}

Yoo, Keun-bong ^{[1
]}

Kim, Doo-soo ^{[1
]}

Kim, Jae-hoon ^{[2
]}

机构：

[1] KEPCO Res Inst, Power Generat Lab, 65 Munji Ro, Taejon 305760, South Korea

[2] Chungnam Natl Univ, Dept Engn Mech, Yuseong Gu, Taejon 305764, South Korea

来源：

STRUCTURAL INTEGRITY AND FAILURE | 2011年 / 275卷

关键词：

gas turbine; thermal exposure; stress-rupture test; mechanical property; GTD111;

D O I：

10.4028/www.scientific.net/AMR.275.31

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

The rotating components in the hot sections of land-based gas turbine are exposed to severe environment during several ten thousand hours at above 1100 degrees C operating temperature. The failure mechanism of the hot gas components would be accompanied by material degradation in the properties of high temperature and creep rupture strength. Many hot gas components in gas turbine are made of Ni-based superalloy because of their high temperature performance. In this work, we surveyed the time and temperature dependent degradation of Ni-based superalloy. We prepared the specimens from GTD111 that are exposed at 871 degrees C and 982 degrees C in 1,000 similar to 10,000 hours. We carried out the mechanical test and microstructural observation.

引用

页码：31 / +

页数：2

共 50 条

[21] Influence of thermal exposure on microstructure and stress rupture properties of a new Re-containing single crystal Ni-based superalloy
Chen-guang Liu
Yun-song Zhao
Jian Zhang
Ding-zhong Tang
Chun-zhi Li
Zhen-ye Zhao
China Foundry, 2018, 15 : 51 - 57
[22] Influence of thermal exposure on microstructure and stress rupture properties of a new Re-containing single crystal Ni-based superalloy
Liu, Chen-guang
Zhao, Yun-song
Zhang, Jian
Tang, Ding-zhong
Li, Chun-zhi
Zhao, Zhen-ye
CHINA FOUNDRY, 2018, 15 (01) : 51 - 57
[23] Effects of non-equilibrium microstructures on microstructure evolution and mechanical properties of laser powder bed fusion IN625 Ni-based superalloy during long-term thermal exposure at 700?C and 750?C
Song, Zhenfeng
Gao, Shuang
Wang, Zhiqiang
Lan, Liang
Hou, Jieshan
He, Bo
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2022, 856
[24] EFFECTS OF WELDING THERMAL CYCLE AND AGING TREATMENT ON THE MICROSTRUCTURE AND MECHANICAL PROPERTY OF A Ni-Fe BASE SUPERALLOY
Wu Dong
Wang Xin
Dong Wenchao
Lu Shanping
ACTA METALLURGICA SINICA, 2014, 50 (03) : 313 - 322
[25] Mechanical Properties and Changes in Microstructure for IN738LC with Thermal Exposure
Yoon, Yong-Keun
Kim, Jae-Hoon
Jeong, Dong-Hee
Yoo, Keun-Bong
TRANSACTIONS OF THE KOREAN SOCIETY OF MECHANICAL ENGINEERS A, 2011, 35 (10) : 1155 - 1160
[26] Microstructural Evolution and Mechanical Evaluation of a Laser-Induced Composite Coating on a Ni-Based Superalloy during Thermal Exposure
Li, Yuebing
He, Yanming
Lu, Chuanyang
Zheng, Wenjian
Yang, Jianguo
Wang, Donghong
Wang, Limei
Sun, Yuan
Gao, Zengliang
MATERIALS, 2019, 12 (09):
[27] Effects of Fe and Ni Additions and Thermal Exposure on the Microstructure and Mechanical Properties of Hypereutectic Al-Si-Cu-Mg Alloy
An, Maohui
Wang, Chenggang
Li, Feng
Wang, Jinguo
Yan, Ruifang
INTERNATIONAL JOURNAL OF METALCASTING, 2025,
[28] Effects of microstructure and lattice misfit on creep life of Ni-based single crystal superalloy during long-term thermal exposure
Gan, Wenyan
Gao, Hangshan
Pei, Haiqing
Wen, Zhixun
INTERNATIONAL JOURNAL OF MATERIALS RESEARCH, 2021, 112 (03) : 203 - 214
[29] Microstructure stability and mechanical properties of a new low cost hot-corrosion resistant Ni-Fe-Cr based superalloy during long-term thermal exposure
Sun, Wen
Qin, Xuezhi
Guo, Jianting
Lou, Langhong
Zhou, Lanzhang
MATERIALS & DESIGN, 2015, 69 : 70 - 80
[30] An Overview of Thermal Exposure on Microstructural Degradation and Mechanical Properties in Ni-Based Single Crystal Superalloys
Zhang, Jian
Lu, Fan
Li, Longfei
MATERIALS, 2023, 16 (05)

← 1 2 3 4 5 →