Fracture behaviors and mechanism of 2D C/SiC-BCx composite under tensile load

被引：31

作者：

Zhang, Weihua ^{[1
]}

Cheng, Laifei ^{[1
]}

Liu, Yongsheng ^{[1
,2
]}

Zhang, Litong ^{[1
]}

Yang, Wenbin ^{[1
]}

Zhou, Shengtian ^{[2
]}

机构：

[1] NW Polytech Univ, Natl Key Lab Thermostruct Composite Mat, Xian 710072, Peoples R China

[2] Shenyang Aeroengine Res Inst, Shenyang 110015, Liaoning, Peoples R China

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2011年 / 530卷

关键词：

Composites; Mechanical properties; Carbides; Engine components; CERAMIC-MATRIX COMPOSITES; SICF-SIBC COMPOSITES; SELF-SEALING MATRIX; OXIDATION BEHAVIOR; MICROSTRUCTURE; ENVIRONMENTS; RESISTANCE; FIBERS; CMCS;

D O I：

10.1016/j.msea.2011.09.089

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Tensile fracture behaviors and mechanisms of 2D C/SiC-BCx composite were investigated. Results showed that the 2D C/SiC-BCx composite exhibited similar tensile strength (about 250 MPa), but different fracture mode and damage evolution compared to that of 2D CNC composite under similar monotonic tensile stress condition at room temperature. The initial modulus and fracture modulus of 20 C/SiC-BCx composite obtained under tensile cyclic loading at RT were about 98.6 GPa and 54.5 GPa, respectively. At high temperatures, the tensile strengths were lower than that at room temperature and behaved as a step-like stress-strain curve. (C) 2011 Elsevier B.V. All rights reserved.

引用

页码：297 / 303

页数：7

共 50 条

[1] Fracture behavior and mechanism of 2D C/SiC-BCx composite at room temperature
Liu, Yongsheng
Cheng, Laifei
Zhang, Litong
Yang, Wenbin
Zhou, Shengtian
Zhang, Weihua
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (03): : 1436 - 1441
[2] Fabrication and mechanical behaviors of 2D C/SiC-BCx composite at room temperature
Liu, Yongsheng
Cheng, Laifei
Zhang, Litong
Yang, Wenbin
Zhou, Shengtian
Zhang, Weihua
JOURNAL OF COMPOSITE MATERIALS, 2012, 46 (10) : 1251 - 1260
[3] Stressed oxidation behaviors of 2D C/SiC-BCx composite under wet oxygen atmosphere
Luan, Xin'gang
Liu, Yongsheng
Yang, Wenbin
Peng, Yuqing
Zhang, Litong
Cheng, Laifei
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2016, 36 (11) : 2673 - 2678
[4] Effect of Temperature on Stress Oxidation Behaviors of 2D C/SiC-BCx Composite in Wet Oxygen Atmosphere
Yongsheng Liu
Litong Zhang
Laifei Cheng
Wenbing Yang
Metallurgical and Materials Transactions A, 2014, 45 : 5699 - 5707
[5] Microstructural evolution and self-healing mechanism of a 2D C/SiC-BCx composite under constant load in static wet oxygen and dynamic combustion atmosphere
Liu, Y. S.
Men, J.
Zhang, L. T.
Cheng, L. F.
Yang, W. B.
Zhang, W. H.
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2015, 66 (02): : 128 - 136
[6] Interlaminar shear behaviors of 2D needled C/SiC composites under compressive and tensile loading
Liang, Xiaoqiang
Gao, Xiguang
Zhang, Huajun
Yu, Guoqiang
Xie, Chuyang
Zhang, Shirong
Song, Yingdong
CERAMICS INTERNATIONAL, 2021, 47 (04) : 4954 - 4962
[7] Modeling the bundle bridging mechanism in 2D SiC/C/SiC composite materials
Drissi-Habti, M
Chermant, JL
Rouby, D
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 1999, 30 (04) : 555 - 559
[8] Fracture behaviors of brittle and ductile 2D carbon structures under uniaxial tensile stress
Wang, Shuaiwei
Fan, Zhaochuan
Cui, Yan
Zhang, Shouren
Yang, Baocheng
Chen, Houyang
CARBON, 2017, 111 : 486 - 492
[9] Failure behavior of 2D C/SiC I-beam under bending load
He, Zongbei
Zhang, Litong
Chen, Bo
Liu, Yongsheng
Liu, Xiaoying
COMPOSITE STRUCTURES, 2015, 132 : 321 - 330
[10] TENSILE FRACTURE MECHANISM OF SILICON IMPREGNATED C/C COMPOSITE
Ohtani, Akio
Goto, Ken
MECHANICAL PROPERTIES AND PERFORMANCE OF ENGINEERING CERAMICS AND COMPOSITES VII, 2013, : 287 - 297

← 1 2 3 4 5 →