Crystallization behavior and origin of c-axis orientation in sol-gel-derived ZnO:Li thin films on glass substrates

Preferentially, c-axis-oriented lithium-doped zinc oxide (ZnO:Li) thin films were prepared on Pyrex borosilicate glass substrates by a sol-gel method starting from zinc acetate dihydrate, lithium chloride, 2-methoxyethanol and monoethanolamine. Decomposition and crystallization behavior of dip-coated amorphous precursor films during postannealing treatments were investigated by thermogravimetry-differential thermal analysis (TG-DTA), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), optical transmittance measurements, field emission scanning electron microscopy (FESEM) and atomic force microscopy (AFM). It was revealed that the films contained the organic compounds at temperatures up to 300 degreesC, which was the key to the transformation from the amorphous to the crystalline state. Thermodynamical consideration of nucleation and crystal growth was made taking account of surface energies of the film and the glass substrate and an interfacial energy between them. Mechanisms underlying the c-axis orientation were proposed based upon the initial orientation due to nucleation and final growth orientation. (C) 2001 Elsevier Science B.V. Ail rights reserved.