Twinning, dynamic recovery and recrystallization in the hot rolling process of twin-roll cast AZ31B alloy

Hot-rolling experiments with a reduction from 10% to 60% in single pass were conducted on AZ31B twin-roll cast sheets. Optical microscope (OM), electron backscattered diffraction (EBSD) tests and transmission electron microscope (TEM) were used to investigate twinning and DRV/DRX behaviors at different stage in the hot-rolling process. Two types of twinning occurred in the initial stage of hot-rolling process. DRV and discontinuous recrystallization dominated at moderate strain while continuous DRX took place homogeneously throughout original grains at the largest strains. Crown Copyright (C) 2011 Published by Elsevier B.V. All rights reserved.