The influence of mechanical stress on cable service life-time

被引：21
作者：
Placek, Vit [1 ]
Kohout, Tomas [1 ]
Kabrt, Jan [1 ]
Jiran, Jindrich [1 ]
机构：
[1] Nucl Res Inst Rez, Rez 25068, Czech Republic
来源：
POLYMER TESTING | 2011年 / 30卷 / 07期
关键词：
Nuclear power plant; Aging; Cable; Life time; LOCA; NUCLEAR-POWER-PLANTS; DSC;
D O I：
10.1016/j.polymertesting.2011.06.005
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
A safety-related cable currently used in nuclear power plants was exposed to accelerated aging to simulate its long-term operation at a temperature of 55 degrees C and a dose rate of 0.2 Gy/h, including loss of coolant accident (LOCA). We studied the influence of excessive mechanical stress on its rate of degradation. Some of the samples were bent and others were pressed, and the aging results were compared with a control sample aged without any mechanical stress. The results have shown a relatively small effect of the mechanical stress applied during the aging on the cable function and LOCA resistance, compared to the results obtained on a cable aged without mechanical stress. (C) 2011 Elsevier Ltd. All rights reserved.
引用
收藏
页码：709 / 715
页数：7
相关论文
共 50 条
[21]   Influence of γ-irradiation and temperature on the mechanical properties of EPDM cable insulation [J].
Sarac, T. ;
Quievy, N. ;
Gusarov, A. ;
Konstantinovic, M. J. .
RADIATION PHYSICS AND CHEMISTRY, 2016, 125 :151-155
[22]   Life-time prediction of a chloroprene rubber (CR) O-ring using intermittent compression stress relaxation (CSR) and time-temperature superposition (TTS) Principle [J].
Jin Hyok Lee ;
Jong Woo Bae ;
Jung Su Kim ;
Tae Jun Hwang ;
Sung Doo Park ;
Sung Han Park ;
Tae Min Yeo ;
Wonho Kim ;
Nam-Ju Jo .
Macromolecular Research, 2011, 19 :555-562
[23]   Associations between Life-Time Physical Activity Levels, Sedentary Time and Health Outcomes among Older Adults [J].
Yilmaz, Fikriye ;
Yilmaz, Atakan .
PROGRESS IN NUTRITION, 2020, 22 :199-205
[24]   Electrode catalysts behavior during direct ethanol fuel cell life-time test [J].
Jiang, LH ;
Sun, GQ ;
Wang, SL ;
Wang, GX ;
Xin, Q ;
Zhou, ZH ;
Zhou, B .
ELECTROCHEMISTRY COMMUNICATIONS, 2005, 7 (07) :663-668
[25]   History-sensitive accumulation rules for life-time prediction under variable creep loading [J].
S. E. Mikhailov ;
I. V. Namestnikova .
Archive of Applied Mechanics, 2011, 81 :1679-1696
[26]   The effect of modifiers on the fluorescence and life-time of Gd3+ ions doped in borate glasses [J].
Kumar, A ;
Rai, DK ;
Rai, SB .
SPECTROCHIMICA ACTA PART A-MOLECULAR AND BIOMOLECULAR SPECTROSCOPY, 2001, 57 (13) :2587-2591
[27]   History-sensitive accumulation rules for life-time prediction under variable creep loading [J].
Mikhailov, S. E. ;
Namestnikova, I. V. .
ARCHIVE OF APPLIED MECHANICS, 2011, 81 (11) :1679-1696
[28]   Incorporating Expected Life-Time into Live Load Factor for RC Structures Using Reliability Analysis [J].
Zadeh, Hany Jawaheri ;
Nanni, Antonio .
ADVANCES IN STRUCTURAL ENGINEERING, 2013, 16 (05) :887-898
[29]   Influence of Mechanical, Thermal, Oxidative and Catalytic Processes on Thickener Structure and Thus on the Service Life of Rolling Bearings [J].
Grebe, Markus ;
Ruland, Michael .
LUBRICANTS, 2022, 10 (05)
[30]   A Study on the Thermal Life-Time Expectation of a NR Rubber Material using Isothermal TGA and TMA [J].
Ahn, WonSool ;
Park, Ki-Ho .
ELASTOMERS AND COMPOSITES, 2009, 44 (03) :269-273
12345