Mixed-mode interfacial fracture toughness for thermal barrier coating

被引:36
作者
Arai, M.
Kajima, Y.
Kishimoto, K.
机构
[1] Cent Res Inst Elect Power Ind, Mat Sci Res Lab, Komae, Tokyo 2018511, Japan
[2] Tokyo Inst Technol, Meguro Ku, Tokyo 1528552, Japan
关键词
coating; multilayers; interface; fracture toughness; mixed-mode;
D O I
10.1016/j.engfracmech.2006.10.021
中图分类号
O3 [力学];
学科分类号
08 ; 0801 ;
摘要
A new interfacial fracture test method was developed for measuring the mixed-mode interfacial fracture toughness of thermal barrier coated material over a wide range of loading phase angles. The principle of this developed method is based on peeling the coating from the substrate due to compressive loading to the coating edge, as forming a shear loading to the interface, and stinging loading such as beam bending, as normal loading to the interface. The complete closed form of the energy release rate and associated complex stress intensity factor for our testing method is shown. An yttria stabilized zirconia (YSZ) coating, which was sprayed thermally on Ni-based superalloy, was tested using the testing device developed here. The results showed that the energy release rate for the coating-interfacial crack increased with loading phase angle, which is defined by tan(-1) for a ratio of stress intensity factor K-2 to K-1. It was noticed that the interfacial energy release rate increasing with mode 11 loading could be mainly associated with the contact shielding effect due to crack surface roughness rubbing together. (C) 2006 Elsevier Ltd. All rights reserved.
引用
收藏
页码:2055 / 2069
页数:15
相关论文
共 20 条
[1]  
[Anonymous], 1996, NATL RES COUNCIL COA, DOI DOI 10.17226/5038
[2]  
Arai M., 2003, Journal of the Society of Materials Science, Japan, V52, P1135, DOI 10.2472/jsms.52.1135
[3]   SMALL-SCALE CRACK BRIDGING AND THE FRACTURE-TOUGHNESS OF PARTICULATE-REINFORCED CERAMICS [J].
BUDIANSKY, B ;
AMAZIGO, JC ;
EVANS, AG .
JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 1988, 36 (02) :167-187
[4]   AN EXPERIMENTAL-STUDY OF THE FRACTURE-RESISTANCE OF BIMATERIAL INTERFACES [J].
CAO, HC ;
EVANS, AG .
MECHANICS OF MATERIALS, 1989, 7 (04) :295-304
[5]   A test specimen for determining the fracture resistarim of bimaterial interfaces [J].
Charalambides, PG ;
Lund, J ;
Evans, AG ;
McMeeking, RM .
JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME, 1989, 56 (01) :77-82
[6]   On the propagation and coalescence of delamination cracks in compressed coatings: with application to thermal barrier systems [J].
Chen, X ;
Hutchinson, JW ;
He, MY ;
Evans, AG .
ACTA MATERIALIA, 2003, 51 (07) :2017-2030
[7]  
CHERPANOV GP, 1987, MECH BRITTLE FRACTUR
[8]   The interface crack [J].
Comninou, Maria .
Journal of Applied Mechanics, Transactions ASME, 1977, 44 (04) :631-636
[9]   Shear strength of a thermal barrier coating parallel to the bond coat [J].
Cruse, TA ;
Dommarco, RC ;
Bastias, PC .
JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1998, 120 (01) :26-32
[10]  
ENGLAND AH, 1965, J APPL MECH JUN, P400