Preparation and characterization of a high surface area of activated carbon from Bambusa vulgaris-Effect of NaOH activation and pyrolysis temperature

被引：24

作者：

Mistar, E. M. ^{[1
]}

Ahmad, S. ^{[1
]}

Muslim, A. ^{[2
]}

Alfatah, T. ^{[3
]}

Supardan, M. D. ^{[2
]}

机构：

[1] Serambi Mekkah Univ, Chem Engn Dept, Banda Aceh, Indonesia

[2] Syiah Kuala Univ, Chem Engn Dept, Banda Aceh, Indonesia

[3] Environm & Forestry Off Aceh Prov, Banda Aceh, Indonesia

来源：

3RD INTERNATIONAL CONFERENCE ON CHEMICAL ENGINEERING SCIENCES AND APPLICATIONS 2017 (3RD ICCHESA 2017) | 2018年 / 334卷

关键词：

D O I：

10.1088/1757-899X/334/1/012051

中图分类号：

TQ [化学工业];

学科分类号：

0817 ;

摘要：

In this study, Bambusa vulgaris was used as raw material of activated carbon. The activated carbon was generated using NaOH as an activating agent. The activated carbon produced with the weight ratio of carbon to NaOH 1:1, 1:2, 1:3 and pyrolysis temperature 600, 700 and 800 degrees C. The experimental result showed that the best characteristic of activated carbon was obtained at weight ratio of carbon to NaOH 1:3 and pyrolysis temperature 800 degrees C.

引用

页数：6

共 10 条

[1]

Arahman N., 2015, ENVIRON TECHNOL, V8, P1

[2] NaOH-activated carbon of high surface area produced from coconut shell: Kinetics and equilibrium studies from the methylene blue adsorption [J].

Cazetta, Andre L. ;

Vargas, Alexandro M. M. ;

Nogami, Eurica M. ;

Kunita, Marcos H. ;

Guilherme, Marcos R. ;

Martins, Alessandro C. ;

Silva, Tais L. ;

Moraes, Juliana C. G. ;

Almeida, Vitor C. .

CHEMICAL ENGINEERING JOURNAL, 2011, 174 (01) :117-125

[3] A new method on producing high surface area activated carbon: The effect of salt on the surface area and the pore size distribution of activated carbon prepared from pistachio shell [J].

Dolas, Hacer ;

Sahin, Omer ;

Saka, Cafer ;

Demir, Halil .

CHEMICAL ENGINEERING JOURNAL, 2011, 166 (01) :191-197

[4] Adsorption of Cd(II), Hg(II) and Zn(II) from aqueous solution using mesoporous activated carbon produced from Bambusa uulgaris striata [J].

Gonzalez, P. G. ;

Pliego-Cuervo, Y. B. .

CHEMICAL ENGINEERING RESEARCH & DESIGN, 2014, 92 (11) :2715-2724

[5] Characterization of mesoporous carbon prepared from date stems by H3PO4 chemical activation [J].

Hadoun, H. ;

Sadaoui, Z. ;

Souami, N. ;

Sahel, D. ;

Toumert, I. .

APPLIED SURFACE SCIENCE, 2013, 280 :1-7

[6]

Prasetyo Y, 2013, UNESA J CHEM, V2, P3

[7]

Setianingsih T, 2008, INDONES J CHEM, V8, P348

[8]

Shofa, 2012, ACTIVATED CARBON BAG

[9] Preparation and characterization of activated carbon from rice bran [J].

Suzuki, R. M. ;

Andrade, A. D. ;

Sousa, J. C. ;

Rollemberg, M. C. .

BIORESOURCE TECHNOLOGY, 2007, 98 (10) :1985-1991

[10] Preparation of high surface area activated carbon from coconut shells using microwave heating [J].

Yang, Kunbin ;

Peng, Jinhui ;

Srinivasakannan, C. ;

Zhang, Libo ;

Xia, Hongying ;

Duan, Xinhui .

BIORESOURCE TECHNOLOGY, 2010, 101 (15) :6163-6169

← 1 →