Resistance to Moisture-Induced Damage of Half-Warm-Mix Asphalt Concrete with Foamed Bitumen

Hot-mix asphalt (HMA) remains the predominant material for pavement surfacing. Mixing is performed at about 180 degrees C, depending on the bitumen used. Environmental concerns in terms of emissions and energy demand are fostering new sustainable technologies in road construction. Warm-mix asphalt (WMA) and half-warm-mix asphalt (HWMA) mixtures meet current expectations in that they are produced at lower temperatures, 100-130 degrees C, ensured by foaming the bitumen with water. The extent of temperature reduction requires that the mixture has adequate moisture and frost resistance, which is particularly important in countries that have a low-temperature climate. Asphalt concrete AC 8 S with 50/70-grade foamed bitumen modified with 0.6 wt.% surface-active agent (SAA) was used in the tests. To provide the AC mixture with the required resistance to climatic factors (water, temperature below 0), hydrated lime was added at 0, 15, 30, and 45 wt.% as limestone filler replacement. The influence of the hydrated lime addition on the air void content and resistance to moisture and frost damage was investigated according to the WT-2 2014 methodology based on EN 12697-12: 2008 and to the modified AASHTO T283 method. The optimum content of hydrated lime for filler replacement was determined through statistical analysis of the test results. With the optimum hydrated lime replacement of 30%, the required level of moisture and frost resistance of HWMA concrete with foamed bitumen is achieved. The results of this study confirmed the suitability of HWMA concrete with foamed bitumen for application in road construction practice.