Effect of Solution Heat Treatment Time on a Rheocast Al-Zn-Mg-Cu Alloy

被引：10
|
作者：
Mazibuko, Nonjabuliso E. [1 ]
Curle, Ulyate A. [1 ]
机构：
[1] CSIR, ZA-0001 Pretoria, South Africa
来源：
LIGHT METALS TECHNOLOGY V | 2011年 / 690卷
关键词：
CSIR-RCS; eutectic phase; intermetallic phases; hardness; EVOLUTION;
D O I：
10.4028/www.scientific.net/MSF.690.343
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
During rheo-high pressure die casting (R-HPDC) of Al-Zn-Mg-Cu alloys a coarse eutectic phase is formed. This eutectic phase is difficult to take into solution because of its size and it would require longer solution heat treatment times. The objective of this work was to determine the time for sufficient dissolution of the eutectic phase in this Al-Zn-Mg-Cu alloy. Solution heat treatment was carried out at 473 degrees C for various time periods and the samples were quenched in water. The samples were then artificially aged at 120 degrees C for 24 hrs. A component of the eutectic was observed to have dissolved and another component transformed to new intermetallic phases for all solution heat treatment times at 473 degrees C.
引用
收藏
页码：343 / 346
页数：4
相关论文
共 50 条
  • [41] Precipitation behavior and mechanical property anisotropy of Al-Zn-Mg-Cu alloy forgings
    Lee, Sang-Hwa
    Shin, Jung Ho
    Lee, Seok-Jae
    Jung, Jae-Gil
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2025, 926
  • [42] Investigation of preparation and properties of Al-Zn-Mg-Cu alloy by metal injection moulding
    Chang, Lingling
    Wu, Mao
    Zhang, Lin
    Meng, Yizhe
    Qu, Xuanhui
    POWDER METALLURGY, 2025,
  • [43] Microstructures and Mechanical Properties of an Al-Zn-Mg-Cu Alloy Processed by Two-Step Aging Treatment
    Wang, Feng
    Gong, Yanli
    Du, Yong
    Song, Min
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2020, 29 (07) : 4404 - 4411
  • [44] Microstructure and Mechanical Properties in Friction Stir Welded Thick Al-Zn-Mg-Cu Alloy Plate
    Qiang, Fei
    Wang, Wen
    Qiao, Ke
    Peng, Pai
    Zhang, Ting
    Guan, Xiao-Hu
    Cai, Jun
    Meng, Qiang
    Zhao, Hua-Xia
    Wang, Kuai-She
    ACTA METALLURGICA SINICA-ENGLISH LETTERS, 2022, 35 (08) : 1329 - 1342
  • [45] Effect of single roll drive cross rolling on the microstructure, crystallographic texture, and mechanical behavior of Al-Zn-Mg-Cu alloy
    Kazemi-Navaee, Amir
    Jamaati, Roohollah
    Aval, Hamed Jamshidi
    ARCHIVES OF CIVIL AND MECHANICAL ENGINEERING, 2022, 22 (01)
  • [46] The Role of Ductility and Work Hardening in Sliding Wear of an Al-Zn-Mg-Cu Alloy
    Zhang, Kexing
    Liu, Dong
    Zhao, Xiaolian
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2022, 75 (03) : 749 - 755
  • [47] Effect of Subcritical Annealing on the Microstructure and Mechanical Properties of a Precipitation-Hardened Al-Zn-Mg-Cu Alloy
    Soyama, Juliano
    Rios, Carlos Triveno
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2021, 30 (02) : 1012 - 1021
  • [48] SiC particulate dispersed composites of an Al-Zn-Mg-Cu alloy: Property comparison with parent alloy
    Dasgupta, R
    Meenai, H
    MATERIALS CHARACTERIZATION, 2005, 54 (4-5) : 438 - 445
  • [49] Effect of combined addition of Zr, Ti and Y on microstructure and tensile properties of an Al-Zn-Mg-Cu alloy
    Li, Jiaheng
    Zhang, Yingbo
    Li, Mojia
    Hu, Yunfeng
    Zeng, Qi
    Zhang, Pu
    MATERIALS & DESIGN, 2022, 223
  • [50] Effects of Mg and Cu on microstructures and properties of spray-deposited Al-Zn-Mg-Cu alloys
    Li, Haichao
    Cao, Fuyang
    Guo, Shu
    Jia, Yandong
    Zhang, Dayue
    Liu, Zuyan
    Wang, Pei
    Scudino, Sergio
    Sun, Jianfei
    JOURNAL OF ALLOYS AND COMPOUNDS, 2017, 719 : 89 - 96
12345