Influences of different prior heat treatments on the microstructural and mechanical properties of Cu-Fe filamentary composites

被引:9
作者
Wu, Z. W. [1 ]
Meng, L. [2 ]
机构
[1] Civil Aviat Univ China, Airport Coll, Tianjin 300300, Peoples R China
[2] Zhejiang Univ, Dept Mat Sci & Engn, Hangzhou 310027, Zhejiang, Peoples R China
关键词
Metals and alloys; Interface; Mechanical properties; Microstructure; ELECTRICAL-CONDUCTIVITY; WIRE-DRAWN; STRENGTH; DEFORMATION; MICROCOMPOSITE; EVOLUTION;
D O I
10.1016/j.jallcom.2011.06.030
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Cu-6 wt.% Fe and Cu-12 wt.% Fe filamentary composites were prepared by casting and cold drawing. And a different heat treatment of quenching and aging or homogenizing was introduced before cold drawing process, respectively. The microstructure was observed and the tensile strength measured for the composites at different drawing strains. The quenching and aging or homogenizing prior to drawing deformation refine the as-cast microstructure and result in the increase in interface density in the drawn microstructure. The drawn alloys with the homogenizing treatment show smaller filament spacing than those with the quenching and aging treatment because homogenizing results in smaller and more dispersive primary Fe dendrites before drawing deformation. The heat treatments can improve the strength of the composites by increasing precipitation strengthening and interface strengthening levels. With the reduction in filament spacing during drawing deformation, the strength of the alloys with smaller initial size of Fe dendrites increases more obviously. Crown Copyright (C) 2011 Published by Elsevier B. V. All rights reserved.
引用
收藏
页码:8917 / 8921
页数:5
相关论文
共 22 条
[1]   Microstructure and strength of wire-drawn Cu-Ag filamentary composites [J].
Benghalem, A ;
Morris, DG .
ACTA MATERIALIA, 1997, 45 (01) :397-406
[2]   Microstructure and strength of Cu-Fe in situ composites after very high drawing strains [J].
Biselli, C ;
Morris, DG .
ACTA MATERIALIA, 1996, 44 (02) :493-504
[3]   Novel Cu-Nb-wires: Processing and characterisation [J].
Botcharova, E ;
Freudenberger, J ;
Gaganov, A ;
Khlopkov, K ;
Schultz, L .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 416 (1-2) :261-268
[4]   Microstructural evolution and its effect on the mechanical properties of Cu-Ag microcomposites [J].
Gaganov, A ;
Freudenberger, J ;
Grünberger, W ;
Schultz, L .
ZEITSCHRIFT FUR METALLKUNDE, 2004, 95 (06) :425-432
[5]   STRENGTHENING IN DEFORMATION-PROCESSED CU-20-PERCENT FE COMPOSITES [J].
GO, YS ;
SPITZIG, WA .
JOURNAL OF MATERIALS SCIENCE, 1991, 26 (01) :163-171
[6]   High strain rate superplasticity of deformation processed Cu-Ag filamentary composites [J].
Hong, SI ;
Kim, PH ;
Choi, YC .
SCRIPTA MATERIALIA, 2004, 51 (02) :95-99
[7]   Microstructural stability and mechanical response of Cu-Ag microcomposite wires [J].
Hong, SI ;
Hill, MA .
ACTA MATERIALIA, 1998, 46 (12) :4111-4122
[8]   Thermo-mechanical processing and properties of Cu-9Fe-1.2Co microcomposite wires [J].
Hong, SI ;
Song, JS ;
Kim, HS .
SCRIPTA MATERIALIA, 2001, 45 (11) :1295-1300
[9]   STRENGTH AND ELECTRICAL-CONDUCTIVITY OF DEFORMATION-PROCESSED CU-15 VOL PCT FE ALLOYS PRODUCED BY POWDER-METALLURGY TECHNIQUES [J].
JERMAN, GA ;
ANDERSON, IE ;
VERHOEVEN, JD .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1993, 24 (01) :35-42
[10]   Effect of aging treatment on microstructure and mechanical properties of Cu-Ag alloys [J].
Lin, J. ;
Meng, L. .
JOURNAL OF ALLOYS AND COMPOUNDS, 2008, 454 (1-2) :150-155