PACVD TiN/Ti-B-N multilayers: from micro- to nano-scale

被引:34
作者
Stoiber, M
Perlot, S
Mitterer, C
Beschliesser, M
Lugmair, C
Kullmer, R
机构
[1] Mat Ctr Leoben, A-8700 Leoben, Austria
[2] Univ Leoben, Dept Phys Met & Mat Testing, A-8700 Leoben, Austria
[3] Rubig GmbH, A-4600 Wels, Austria
[4] CoKG, A-4600 Wels, Austria
关键词
multilayers; plasma-assisted chemical vapor deposition (PACVD); TiN; Ti-B-N; friction;
D O I
10.1016/j.surfcoat.2003.09.025
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Multilayer coatings with compositionally modulated structures in the nanometer range such as superlattices often show improved mechanical properties compared to homogenous materials. Various physical vapor deposition (PVD) methods have been utilized to deposit superlattice coatings, while chemical vapor deposition (CVD) is not suitable due to interdiffusion at high deposition temperatures. The aim of this work was to investigate the potential of plasma-assisted chemical vapor deposition (PACVD) for multilayers with extension to layer thicknesses in the nanometer range. TiN/Ti-B-N multilayers have been deposited in an industrially sized deposition chamber to optimize mechanical and tribological properties. Different layer numbers (4, 16, 32, 64, 128 and 300) of TiN and a 23 at.% B containing Ti-B-N coating have been alternately deposited by varying gas flow rates resulting in a total coating thickness of 2-3 mum. Electron energy-loss spectroscopy (EELS) measurements showed separated 5-nm thick layers for a total of 300 layers. A decrease in compressive stress has been observed for a decreasing individual layer thickness, which enhanced coating adhesion on tool steels. For the 4-layer coating, the friction behavior is determined by the higher chlorine containing low-friction TiN layer resulting in a constant steady-state friction coefficient of 0.2, whereas stable values of approximately 0.8 were reached for higher layer numbers. The optimum wear resistance was obtained for 128 layers, which is attributed to a combination of well-defined interfaces and moderate compressive stresses. (C) 2003 Elsevier B.V. All rights reserved.
引用
收藏
页码:348 / 354
页数:7
相关论文
共 21 条
[1]  
[Anonymous], HDB HARD COATINGS
[2]   Overview no. 130 - Size effects in materials due to microstructural and dimensional constraints: A comparative review [J].
Arzt, E .
ACTA MATERIALIA, 1998, 46 (16) :5611-5626
[3]  
BARNETT SA, 1993, PHYS THIN FILMS
[4]   Hard coatings produced by PACVD applied to aluminium die casting [J].
Heim, D ;
Holler, F ;
Mitterer, C .
SURFACE & COATINGS TECHNOLOGY, 1999, 116 :530-536
[5]   CHARACTERIZATION OF MICROSTRUCTURE AND INTERFACES IN TIC-TIB2 COATINGS [J].
HILZ, G ;
HOLLECK, H .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1991, 139 :268-275
[6]  
Holleck H, 1995, SURF COAT TECH, V76, P328, DOI 10.1016/0257-8972(95)02555-3
[7]   PREPARATION AND BEHAVIOR OF WEAR-RESISTANT TIC/TIB2, TIN/TIB2 AND TIC/TIN COATINGS WITH HIGH AMOUNTS OF PHASE BOUNDARIES [J].
HOLLECK, H ;
SCHULZ, H .
SURFACE & COATINGS TECHNOLOGY, 1988, 36 (3-4) :707-714
[8]   MULTILAYER COATINGS - INFLUENCE OF FABRICATION PARAMETERS ON CONSTITUTION AND PROPERTIES [J].
HOLLECK, H ;
LAHRES, M ;
WOLL, P .
SURFACE & COATINGS TECHNOLOGY, 1990, 41 (02) :179-190
[9]   Recent progress in large scale manufacturing of multilayer/superlattice hard coatings [J].
Hovsepian, PE ;
Lewis, DB ;
Münz, WD .
SURFACE & COATINGS TECHNOLOGY, 2000, 133 :166-175
[10]   Preparation and concentration distribution of multicomponent hard coatings [J].
Jehn, HA ;
Rother, B .
INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 1996, 14 (1-3) :87-95