Influence of anodization on the fatigue strength of 7050-T7451 aluminium alloy

被引：44

作者：

Camargo, A. ^{[1
]}

Voorwald, H. ^{[1
]}

机构：

[1] UNESP, FEG, DMT, Fatigue & Aeronaut Mat Res Grp, BR-12516410 Guaratingueta, SP, Brazil

来源：

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES | 2007年 / 30卷 / 11期

关键词：

7050-T7451 aluminium alloy; anodization; coatings; fatigue; residual stress; shot peening;

D O I：

10.1111/j.1460-2695.2007.01169.x

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

In recent years, with higher demand for improved quality and corrosion resistance, recovered substrates have been extensively used. Consequently residual stresses originated from these coatings reduce the fatigue strength of a component. Due to this negative influence occasioned by corrosion resistance protective coatings, an effective process like shot peening must be considered to improve the fatigue strength. The shot peening treatment pushes the crack sources beneath the surface in most of medium and high cycle cases due to the compressive residual stress field (CRSF) induced. The aim of this study was to evaluate the influence on the fatigue life of anodic films grown on 7050-T7451 aluminium alloy by sulphuric acid anodizing, chromic acid anodizing and hard anodizing. The influence on the rotating and reverse bending fatigue strength of anodic films grown on the aluminium alloy is to degrade the stress life fatigue performance of the base material. A consistent gain in fatigue life in relation to the base material was obtained through the shot peening process in coated specimens, associated to a residual stress field compressive near the surface, useful to avoid fatigue crack nucleation and delay or even stop crack propagation.

引用

页码：993 / 1007

页数：15

共 15 条

[1]

Buffoli A, 1995, ADVANCES IN THERMAL SPRAY SCIENCE AND TECHNOLOGY, P671

[2] Analysis of the effects of controlled shot peening on fatigue damage of high strength aluminium alloys [J].

Curtis, S ;

de los Rios, ER ;

Rodopoulos, CA ;

Levers, A .

INTERNATIONAL JOURNAL OF FATIGUE, 2003, 25 (01) :59-66

[3] Influence of anodization on the fatigue life of WE43A-T6 magnesium [J].

Eifert, AJ ;

Thomas, JP ;

Rateick, RG .

SCRIPTA MATERIALIA, 1999, 40 (08) :929-935

[4] Fatigue behavior of a quenched and tempered AISI 4340 steel coated with an electroless Ni-P deposit [J].

Garcés, Y ;

Sánchez, H ;

Berríos, J ;

Pertuz, A ;

Chitty, J ;

Hintermann, H ;

Puchi, ES .

THIN SOLID FILMS, 1999, 355 :487-493

[5] An approach for prediction of fatigue strength of shot peened components [J].

Guagliano, M ;

Vergani, L .

ENGINEERING FRACTURE MECHANICS, 2004, 71 (4-6) :501-512

[6] Study of the residual stress state during plastic deformation under uniaxial tension in a 5.0Cr and 0.5Mo steel [J].

Gurova, T ;

Teodosio, JR ;

Rebello, JMA ;

Monin, V .

SCRIPTA MATERIALIA, 1997, 36 (09) :1031-1035

[7] The effect of residual stress in HVOF tungsten carbide coatings on the fatigue life in bending of thermal spray coated aluminum [J].

McGrann, RTR ;

Greving, DJ ;

Shadley, JR ;

Rybicki, EF ;

Bodger, BE ;

Somerville, DA .

JOURNAL OF THERMAL SPRAY TECHNOLOGY, 1998, 7 (04) :546-552

[8]

Nascimento MP, 2001, PLAT SURF FINISH, V88, P84

[9] Effects of tungsten carbide thermal spray coating by HP/HVOF and hard chromium electroplating on AISI 4340 high strength steel [J].

Nascimento, MP ;

Souza, RC ;

Miguel, IM ;

Pigatin, WL ;

Voorwald, HJC .

SURFACE & COATINGS TECHNOLOGY, 2001, 138 (2-3) :113-124

[10] Fatigue behavior of a 4140 steel coated with a NiMoAl deposit applied by HVOF thermal spray [J].

Padilla, K ;

Velásquez, A ;

Berríos, JA ;

Cabrera, ESP .

SURFACE & COATINGS TECHNOLOGY, 2002, 150 (2-3) :151-162

← 1 2 →