Phase transformation behaviors and mechanical properties of TiNiMo shape memory alloys

被引：30

作者：

Liu, FS ^{[1
]}

Ding, Z ^{[1
]}

Li, Y ^{[1
]}

Xu, HB ^{[1
]}

机构：

[1] Beijing Univ Aeronaut & Astronaut, Sch Mat Sci & Engn, Beijing 100083, Peoples R China

来源：

INTERMETALLICS | 2005年 / 13卷 / 3-4期

关键词：

martensitic transformations;

D O I：

10.1016/j.intermet.2004.07.024

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

Phase transformation behaviors and mechanical properties of TiNiMo shape memory alloys have been investigated. It was found that the martensite transformation temperatures decrease drastically with increasing Mo content, while the R phase transformation temperatures vary slightly. Ti50M49.5Mo0.5 and Ti50Ni49Mo1.0 alloys exhibit good workability with lower ay C I followed by drastically plastic deformation due to slip. Ti50Ni48Mo2.0 alloy with moderate martensite transformation temperature, much higher yield strength and fracture strength measured to be 589 and 799 MPa, respectively, as well as Ti50Ni48.5Mo1.5 alloy with appropriate martensite transformation temperature and excellent mechanical properties, are very promising for use as coupling materials. (c) 2004 Elsevier Ltd. All rights reserved.

引用

页码：357 / 360

页数：4