Measurement of the elastic modulus of a plasma-sprayed thermal barrier coating using spherical indentation

被引:13
作者
Eskner, M [1 ]
Sandström, R
机构
[1] Royal Inst Technol, Dept Mat Sci & Engn, SE-10044 Stockholm, Sweden
[2] Royal Inst Technol, Brinell Ctr, SE-10044 Stockholm, Sweden
关键词
elastic modulus; thermal barrier coating; spherical indentation;
D O I
10.1016/j.surfcoat.2003.06.018
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Failure in plasma-sprayed thermal barrier coatings systems mostly takes place in the ceramic topcoat or at the interface between the topcoat and the bondcoat. The failure normally occurs by spallation of the topcoat at shutdown operations from high temperatures where compressive thermal-mismatch stresses are induced in the topcoat. In order to analyse the residual stresses, knowledge about the elastic modulus for the different components in the coating system is required. In this work, a spherical indentation method has been used for room-temperature measurement of the elastic modulus of both the topcoat (300-mum-thick air-plasma sprayed ZrO2-8wt,%Y2O3) and the bondcoat (150-mum-thick air-plasma sprayed Ni-23Co-17Cr-12Al-0.5Y). This method gives the compressive modulus, which for the top-coat may be more adequate as it has different modulus in tensile and compressive stress states due to its microstructure. Measurements were made on specimens in as-coated condition and after heat treatment (1500 h at 1000 degreesC). A significant increase in the elastic modulus of the bondcoat was observed as a result from the heat treatment, from 137 to 226 GPa, which is explained by the internal oxidation at the initial weak inter-splat regions. A sintering effect and a change in the elastic modulus were also observed for the topcoat as a result of the beat-treatment, where the elastic modulus increased from 38 to 60 GPa. (C) 2003 Elsevier B.V. All rights reserved.
引用
收藏
页码:165 / 171
页数:7
相关论文
共 18 条
[1]   Instrumented spherical micro-indentation of plasma-sprayed coatings [J].
Alcalá, J ;
Gaudette, F ;
Suresh, S ;
Sampath, S .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 316 (1-2) :1-10
[2]   The evolution of thermal barrier coatings - status and upcoming solutions for today's key issues [J].
Beele, W ;
Marijnissen, G ;
van Lieshout, A .
SURFACE & COATINGS TECHNOLOGY, 1999, 120 :61-67
[3]   AN ANALYSIS OF FULLY PLASTIC BRINELL INDENTATION [J].
BIWA, S ;
STORAKERS, B .
JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 1995, 43 (08) :1303-1333
[4]  
Choi SR, 1998, CERAM ENG SCI PROC, V19, P293
[5]   Measurement of the ductile-to-brittle transition temperature in a nickel aluminide coating by a miniaturised disc bending test technique [J].
Eskner, M ;
Sandström, R .
SURFACE & COATINGS TECHNOLOGY, 2003, 165 (01) :71-80
[6]   Mechanisms controlling the durability of thermal barrier coatings [J].
Evans, AG ;
Mumm, DR ;
Hutchinson, JW ;
Meier, GH ;
Pettit, FS .
PROGRESS IN MATERIALS SCIENCE, 2001, 46 (05) :505-553
[7]   THE DURABILITY AND PERFORMANCE OF COATINGS IN GAS-TURBINE AND DIESEL-ENGINES [J].
FAIRBANKS, JW ;
HECHT, RJ .
MATERIALS SCIENCE AND ENGINEERING, 1987, 88 :321-330
[8]  
GOWARD GW, 1970, JOM-J MIN MET MAT S, V22, P31
[9]   SURVIVABILITY OF THERMAL BARRIER COATINGS [J].
HERMAN, H ;
SHANKAR, NR .
MATERIALS SCIENCE AND ENGINEERING, 1987, 88 :69-74
[10]  
Johnson KL., 1985, CONTACT MECH