Layered zinc hydroxide salts: Delamination, preferred orientation of hydroxide lamellae, and formation of ZnO nanodiscs

Delamination of layered zinc hydroxide salts (LZH) into hydroxide layers provides nanobuilding blocs of a two-dimensional anisotropy. The methodology, extent of delamination, the size and stability of hydroxide lamellae are described in detail. The ability of lamellae to restack to form oriented hydroxide films depends on the solvent, original LZH salt, and conditions used for delamination. The most interesting results were obtained using LZH intercalated with dodecyl sulfate anions and LZH nitrate delaminated in butanol at 60 degrees C and in formamide at room temperature, respectively. The former method produces hydroxide lamellae of a lateral size of ca. 10-20 nm. The inner structure of the hydroxide layers is conserved and separated lamellae restack to the original layered structure of LZH dodecyl sulfate. The latter method yields lamellae with a size decreasing from 73.3 nm to 10 nm after a 2-week aging, while their thickness is nearly constant (2.6-3.8 nm). However, the use of formamide is complicated by the formation of Zn(II) formate. The major part of LZH intercalated with dodecyl sulfate anions is transformed during the delamination procedure to anisotropic ZnO nanoparticles, either needle-like particles prolonged in the [0 0 1] direction or disc-like particles flattened along the (0 0 1) plane. (C) 2011 Elsevier Inc. All rights reserved.