Thermodynamic analysis of interactions between Ti-Al alloys and oxide ceramics

被引：29

作者：

Cui Ren-jie ^{[1
]}

Tang Xiao-xia ^{[1
]}

Gao Ming ^{[1
]}

Zhang Hu ^{[1
]}

Gong Sheng-kai ^{[1
]}

机构：

[1] Beihang Univ, Sch Mat Sci & Engn, Key Lab Aerosp Mat & Performance, Minist Educ, Beijing 100191, Peoples R China

来源：

TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA | 2012年 / 22卷 / 04期

关键词：

Ti alloys; thermodynamics; oxide ceramics; interaction; MOLD MATERIALS; REFRACTORIES; TITANIUM;

D O I：

10.1016/S1003-6326(11)61261-2

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The thermodynamics of interactions between various oxides (CaO, MgO, Al2O3 and Y2O3) and molten Ti and Ti alloys was investigated. The dissolution mechanism of oxides in molten Ti alloys was provided and the stability of oxides in molten Ti alloys was investigated and predicted by thermodynamic analysis. Interactions between oxides and Ti-Al melts were studied by oxide crucible melting experiments. By quantitative analysis, it is indicated that impurity contents in alloys are proportionally decreased with increasing the Al content in alloys and decreasing the melt temperature, which is in agreement with the results of the predicting thermodynamic stability.

引用

页码：887 / 894

页数：8

共 21 条

[1] Influence of superheating on casting of γ-TiAl [J].

Barbosa, Joaquim ;

Ribeiro, C. Silva ;

Monteiro, A. Caetano .

INTERMETALLICS, 2007, 15 (07) :945-955

[2] An overview on the use of titanium in the aerospace industry [J].

Boyer, RR .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1996, 213 (1-2) :103-114

[3] Thermodynamic description of the Ti-O system using the associate model for the liquid phase [J].

Cancarevic, M. ;

Zinkevich, M. ;

Aldinger, F. .

CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2007, 31 (03) :330-342

[4]

Chen YY, 2006, T NONFERR METAL SOC, V16, pS1910

[5]

Das K, 2002, J PHASE EQUILIB, V23, P525

[6]

DING Hong-sheng, 1999, J HARBIN I TECHNOLOG, V6, P56

[7]

DING XY, 1994, ACTA METALLURGICA B, V30, P444

[8]

GUO Jing-jie, 1998, THEMODYNAMIC KINETIC

[9]

HUANG Xi-gu, 1989, METALLURGICAL PRINCI

[10] A study of two refractories as mould materials for investment casting TiAl based alloys [J].

Jia, Q. ;

Cui, Y. Y. ;

Yang, R. .

JOURNAL OF MATERIALS SCIENCE, 2006, 41 (10) :3045-3049

← 1 2 3 →