The tensile behavior of GH3535 superalloy at elevated temperature

被引:67
作者
Han, F. F. [1 ]
Zhou, B. M. [1 ]
Huang, H. F. [1 ]
Leng, B. [1 ]
Lu, Y. L. [1 ]
Dong, J. S. [2 ]
Li, Z. J. [1 ]
Zhou, X. T. [1 ]
机构
[1] Chinese Acad Sci, Shanghai Inst Appl Phys, Thorium Molten Salts Reactor Ctr, Beijing 100864, Peoples R China
[2] Chinese Acad Sci, Inst Met Res, Superalloy Div, Beijing 100864, Peoples R China
基金
中国国家自然科学基金;
关键词
Alloys; Mechanical properties; Microstructure; Carbides; SINGLE-CRYSTAL SUPERALLOY; STRAIN-RATE SENSITIVITY; LOW-CYCLE FATIGUE; ACTIVATION-ENERGY; STRESS ANOMALIES; SERRATED FLOW; ALLOYS; MECHANISM; MODEL;
D O I
10.1016/j.matchemphys.2016.07.001
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The tensile behavior of GH3535 alloy has been investigated at strain rates of 8.33 x 10(-5)/s(-1) -8.33 x 10(-3)/s(-1), in the temperature range of 25-800 degrees C. The results showed that the ultimate tensile strength was decreased with increasing temperature and increased with rising strain rate, whereas the yield strength kept almost a constant value at the temperature range from 550 to 800 degrees C in all strain rates test. The formation of M12C carbides at the grain boundary during the tension process played an important role in increasing the yield strength of the alloy at elevated temperatures. But inhomogeneous deformation at 650 degrees C resulted in the minimum ductility of the alloy. Additionally, various types of serrations were noticed on the stress-strain curves for the alloy tested in the temperature range of 500 - 800 degrees C. Normal Portevin-Le Chatelier (PLC) effect and positive strain rate sensitivity were observed in this alloy. Type A and A + B serrations were presented to stress-strain curves at temperatures below 650 degrees C, whereas type C serration was noticed when the temperature rose above 650 degrees C. The analysis suggested that the interactions between substitutional solutes migration and mobile dislocations were the main reason for the serrated flow behavior in this alloy. (C) 2016 Elsevier B.V. All rights reserved.
引用
收藏
页码:22 / 31
页数:10
相关论文
共 33 条
  • [1] Effect of temperature on tensile behavior of Ni-Cr-W based superalloy
    Bai, Guanghai
    Li, Jinshan
    Hu, Rui
    Tang, Zengwu
    Xue, Xiangyi
    Fu, Hengzhi
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (4-5): : 1974 - 1978
  • [2] Yield strength anomaly in B2-ordered feal alloys: Role of boron
    Calonne, O
    Fraczkiewicz, A
    Louchet, F
    [J]. SCRIPTA MATERIALIA, 2000, 43 (01) : 69 - 75
  • [3] GRAIN-BOUNDARY SELF-DIFFUSION OF CR-51 AND FE-59 IN AUSTENITIC NI-FE-CR ALLOYS
    CERMAK, J
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1991, 148 (02): : 279 - 287
  • [4] Investigation of the Dynamic Strain Aging and Mechanical Properties in Alloy-625 with Different Microstructures
    Chatterjee, Arnomitra
    Sharma, Garima
    Tewari, R.
    Chakravartty, J. K.
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2015, 46A (03): : 1097 - 1107
  • [5] Dynamic strain aging in a new Ni-Co base superalloy
    Cui, C. Y.
    Gu, Y. F.
    Yuan, Y.
    Harada, H.
    [J]. SCRIPTA MATERIALIA, 2011, 64 (06) : 502 - 505
  • [6] Dynamic strain ageing in Ni-base superalloy 720Li
    Gopinath, K.
    Gogia, A. K.
    Kamat, Sn.
    Ramamurty, U.
    [J]. ACTA MATERIALIA, 2009, 57 (04) : 1243 - 1253
  • [7] Activation energy calculations for discontinuous yielding in Inconel 718SPF
    Hale, CL
    Rollings, WS
    Weaver, ML
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2001, 300 (1-2): : 153 - 164
  • [8] ON THE MECHANISM OF DELAYED DISCONTINUOUS PLASTIC-FLOW IN AN AGE-HARDENED NICKEL-ALLOY
    HAYES, RW
    HAYES, WC
    [J]. ACTA METALLURGICA, 1982, 30 (07): : 1295 - 1301
  • [9] Tensile deformation behavior of a nickel based superalloy at different temperatures
    Hrutkay, K.
    Kaoumi, D.
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 599 : 196 - 203
  • [10] Comparison of low-cycle fatigue behaviors between two nickel-based single-crystal superalloys
    Li, P.
    Li, Q. Q.
    Jin, T.
    Zhou, Y. Z.
    Li, J. G.
    Sun, X. F.
    Zhang, Z. F.
    [J]. INTERNATIONAL JOURNAL OF FATIGUE, 2014, 63 : 137 - 144