High cycle fatigue behavior and numerical evaluation of Alloy 690TT steam generator tube

被引：17

作者：

Li, Zhenhua ^{[1
]}

Wang, Xinyu ^{[1
]}

Wang, Junping ^{[2
]}

Lu, Yonghao ^{[1
]}

Shoji, Tetsuo ^{[1
]}

机构：

[1] Univ Sci & Technol Beijing, Natl Ctr Mat Serv Safety, Beijing 100083, Peoples R China

[2] Beijing Univ Civil Engn & Architecture, Sch Sci, Beijing 102616, Peoples R China

来源：

INTERNATIONAL JOURNAL OF FATIGUE | 2020年 / 137卷 / 137期

关键词：

High cycle fatigue; Alloy; 690TT; Numerical evaluation; Fatigue life; Tubular specimen; STRAIN; PROPAGATION; CRACKING; STRESS; DAMAGE; ZONE; LEAD;

D O I：

10.1016/j.ijfatigue.2020.105662

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

High cycle fatigue behavior of Alloy 690TT steam generator (SG) tube under different maximum stresses was investigated at stress ratio R = 0.1 through experimental and numerical evaluation. The morphology of fatigue fracture surface was observed by SEM, and the crack initiation and propagation mechanism of Alloy 690TT SG tube was analyzed. The fatigue crack of Alloy 690TT SG tube initiated at the intrados surface edge, then propagated along the direction of maximum shear stress and penetrated through the side of the specimen, and finally transient fracture occurred in the direction perpendicular to the loading axis. With the increase of maximum stress, the number of fatigue crack initiation sources increased, but they were all distributed on the edge of the intrados surface, and a large number of persistent slip bands (PSBs) were formed on the intrados surface. The fracture mechanism of the tubular specimen was different from that of the bar specimen, and its fracture mode affected the life evaluation of the tubular specimen. The finite element analysis software ABAQUS and advanced fatigue durability analysis software FE-SAFE were first used to evaluate the fatigue life of Alloy 690TT SG tube. Compared with the experimental results, the error in predicting fatigue life by numerical method was acceptable.

引用

页数：9

共 22 条

[11] CRACK PROPAGATION IN HIGH STRESS FATIGUE [J].

LAIRD, C ;

SMITH, GC .

PHILOSOPHICAL MAGAZINE, 1962, 7 (77) :847-&

[12] Effects of scratching on corrosion and stress corrosion cracking of Alloy 690TT at 58 °C and 330 °C [J].

Meng, Fanjiang ;

Wang, Jianqiu ;

Han, En-Hou ;

Ke, Wei .

CORROSION SCIENCE, 2009, 51 (11) :2761-2769

[13]

MINER MA, 1945, J APPL MECH-T ASME, V12, pA159

[14] Fatigue crack initiation and propagation in re-entrant auxetic cellular structures [J].

Ncemer, Branko ;

Kramberger, Janez ;

Vuherer, Tomaz ;

Glodez, Srecko .

INTERNATIONAL JOURNAL OF FATIGUE, 2019, 126 :241-247

[15] High-cycle fatigue behavior of low-C medium-Mn high strength steel with austenite-martensite submicron-sized lath-like structure [J].

Qi, X. Y. ;

Du, L. X. ;

Hu, J. ;

Misra, R. D. K. .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2018, 718 :477-482

[16] Characterization of the crack initiation and propagation in Alloy 600 with a cold-worked surface [J].

Shen, Zhao ;

Chen, Kai ;

Tweddle, David ;

He, Guanze ;

Arioka, Koji ;

Lozano-Perez, Sergio .

CORROSION SCIENCE, 2019, 152 :82-92

[17] Corrosion fatigue behavior of Alloy 690 steam generator tube in borated and lithiated high temperature water [J].

Tan, Jibo ;

Wu, Xinqiang ;

Han, En-Hou ;

Ke, Wei ;

Liu, Xiaoqiang ;

Meng, Fanjiang ;

Xu, Xuelian .

CORROSION SCIENCE, 2014, 89 :203-213

[18] Effects of crack tip plastic zone on corrosion fatigue cracking of alloy 690(TT) in pressurized water reactor environments [J].

Xiao, J. ;

Qiu, S. Y. ;

Chen, Y. ;

Fu, Z. H. ;

Lin, Z. X. ;

Xu, Q. .

JOURNAL OF NUCLEAR MATERIALS, 2015, 456 :120-124

[19] Damage mechanism of Alloy 690TT mated with Type 304 stainless steel during fretting wear in partial slip regime [J].

Xin, Long ;

Luo, Huijuan ;

Han, Junling ;

Lu, Yonghao ;

Shoji, Tetsuo .

MATERIALS CHARACTERIZATION, 2017, 132 :284-292

[20] Investigation of fatigue damage to welded joints under variable amplitude loading spectra [J].

Zhang, Yan-Hui ;

Maddox, S. J. .

INTERNATIONAL JOURNAL OF FATIGUE, 2009, 31 (01) :138-152

← 1 2 3 →