Influence of process parameters for induction hardening on residual stresses

被引:64
作者
Kristoffersen, H [1 ]
Vomacka, P [1 ]
机构
[1] Swedish Inst Prod Engn Res, IVF, SE-43153 Molndal, Sweden
关键词
heat treatments; machining; fatigue; X-ray analysis;
D O I
10.1016/S0261-3069(01)00033-4
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Fatigue behaviour of induction hardened parts is largely dependent on the correct combination of hardening depth and the magnitude and distribution of residual compressive stresses in the surface layer. The objective of this work was to study experimentally the residual stresses at the surface layer of induction hardened cylindrical specimens. Two microstructures, quenchcd-tempered and normalised were investigated. The process parameters of induction hardening were varied to give a constant hardness penetration depth. The residual stresses were measured using the X-ray diffraction method. The investigated induction hardened samples showed a constant biaxial residual stress-state at the surface. The directions of the principal stresses deviated slightly from the defined circumferential and longitudinal directions. However, the shear stresses at the surface were of a small magnitude. This experimental investigation showed that the process parameters of induction hardening influence the residual stress-state of hardened parts to a great extent. (C) 2001 Elsevier Science Ltd. All rights reserved.
引用
收藏
页码:637 / 644
页数:8
相关论文
共 16 条
[1]  
CUNNINGHAM JL, 1999, J MATER ENG PERFORM, V8, P401
[2]   SURFACE DURABILITY OF INDUCTION-HARDENED 0. 45 PER CENT CARBON STEEL AND ITS OPTIMUM CASE DEPTH. [J].
Fujita, Komei ;
Yoshida, Akira ;
Nakase, Kazuo .
Bulletin of the JSME, 1979, 22 (169) :994-1000
[3]  
GRUM J, 1997, P 17 ASM HEAT TREAT, P629
[4]   EFFECT OF RESIDUAL-STRESS ON FATIGUE-STRENGTH OF INDUCTION-HARDENED STEEL [J].
HAYAMA, T .
BULLETIN OF THE JSME-JAPAN SOCIETY OF MECHANICAL ENGINEERS, 1975, 18 (125) :1194-1200
[5]  
HAYASHI K, 1969, J MAT SCI JPN, V18, P1100
[6]  
LIN R, 1992, P 3 ECRS FRANKF MAIN, P505
[7]  
LODE W, 1980, HART TECH MITT, V35, P148
[8]  
Lu J, 1996, Handbook of measurement of residual stresses
[9]  
MOORE MG, 1956, M SAE RES STRESS COM
[10]  
Noyan I. C., 1987, RESIDUAL STRESS MEAS