Behavior of small cracks under negative stress ratio fatigue loading

被引：5

作者：

Roiko, A. ^{[1
]}

Solin, J. ^{[1
]}

Hanninen, H. ^{[2
]}

机构：

[1] Finland Ltd, VTT Tech Res Ctr, POB 1000, FI-20044 Espoo, Finland

[2] Aalto Univ, Sch Engn, Espoo, Finland

来源：

INTERNATIONAL JOURNAL OF FATIGUE | 2017年 / 104卷

关键词：

GROWTH;

D O I：

10.1016/j.ijfatigue.2017.07.006

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

In this paper we analyze growth of small cracks initiated from microscopic notches and loaded near the growth threshold under different stress ratios. The results of in-situ optical measurements during high cycle fatigue testing show that small cracks initiate and grow quickly after which there is a long period of slow growth until the large crack growth threshold is reached. The crack growth rate data from different loading ratios indicates that the positive portion of the stress amplitude or the maximum stress intensity factor can be used to compare crack growth rates. The test data also shows that increasing only the compressive stress portion of the loading will cause an arrested small crack to grow again. (C) 2017 Elsevier Ltd. All rights reserved.

引用

页码：379 / 388

页数：10

共 16 条

[1] Reconsiderations of fatigue crack growth at negative stress ratios: Finite element analyses [J].

Benz, C. ;

Sander, M. .

ENGINEERING FRACTURE MECHANICS, 2015, 145 :98-114

[2]

Beretta S, 1999, EXTREMES, V2, P123

[3]

Elber W., 1970, Engineering Fracture Mechanics, V2, P37, DOI 10.1016/0013-7944(70)90028-7

[4]

Elber W., 1971, Damage tolerance in aircraft structures, P230, DOI DOI 10.1520/STP486-EB

[5] FATIGUE CRACK-GROWTH UNDER COMPRESSIVE LOADING [J].

FLECK, NA ;

SHIN, CS ;

SMITH, RA .

ENGINEERING FRACTURE MECHANICS, 1985, 21 (01) :173-+

[6] FATIGUE-CRACK GROWTH IN DUCTILE MATERIALS UNDER CYCLIC COMPRESSIVE LOADING [J].

HERMANN, R .

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1994, 17 (01) :93-103

[7]

Kardomateas GA, 1998, FATIGUE FRACT ENG M, V21, P411, DOI 10.1046/j.1460-2695.1998.00539.x

[8] Fatigue crack growth under compressive loading [J].

Kasaba, K ;

Sano, T ;

Kudo, S ;

Shoji, T ;

Katagiri, K ;

Sato, T .

JOURNAL OF NUCLEAR MATERIALS, 1998, 258 :2059-2063

[9]

Murakami Y., STRESS INTENSITY FAC

[10]

Murakami Y, 1986, J SOC MATER SCI JPN, P911

← 1 2 →