Comparison of optical and crystal properties of three translucent yttria-stabilized tetragonal zirconia polycrystals with those of lithium disilicate glass-ceramic material

Background/purpose: Among the ceramic materials used for all-ceramic crowns, zirconia has high biocompatibility and favorable mechanical properties, but its main drawbacks include low translucency and stress-induced phase transformation. To stabilize high-strength tetragonal zirconia polycrystal (TZP), 3-5 mol% yttria is usually added to prepare yttria-stabilized TZP (Y-TZP). In this study, the optical properties of three commercial Y-TZP ceramics were compared with those of the clinically available glass-ceramic material of lithium disilicate, and the relationship between translucency and crystal properties was analyzed in vitro. Materials and methods: Twelve 5-mm-thick standardized disks were prepared from three Y-TZP ceramics and one lithium disilicate block. Absolute translucency was measured using a spectrophotometer with an integrating sphere. X-ray diffraction was used to quantify the main structural parameters (i.e., preferred plane, quantitative phase, and grain size) of Y-TZP crystals. Results: The product-dominated phase of Y-TZP exhibited a tetragonal lattice pattern, and the preferred planes had minor variations. The diffraction patterns of the three Y-TZP ceramics demonstrated minor effects on translucency, without significant differences (p > 0.05). The grain size of 54-70 nm was negatively related to translucency in Y-TZP. Lithium disilicate specimens had significantly higher translucency than the three Y-TZP specimens (p < 0.001). Conclusion: Grain size reduction played an essential role in developing highly translucent YTZP ceramics. The three Y-TZP ceramics were essentially opaque but exhibited poorer translucency than lithium disilicate in terms of esthetics. (c) 2021 Association for Dental Sciences of the Republic of China. Publishing services by Elsevier B.V. This is an open access article under the CC BY-NC-ND license (http:// creativecommons.org/licenses/by-nc-nd/4.0/).