Microstructure and shear strength of brazed joints between Ti(C,N)-based cermet and steel with Cu-Ag-Ti filler metal

被引：12

作者：

Jing, Yong ^{[1
]}

Yang, Qingqing ^{[1
]}

Xiong, Weihao ^{[1
]}

Huang, Bin ^{[1
]}

Li, Baolong ^{[1
]}

Zhang, Man ^{[1
]}

机构：

[1] Huazhong Univ Sci & Technol, State Key Lab Mat Format & Dies & Moulds Technol, Wuhan 430074, Peoples R China

来源：

JOURNAL OF ALLOYS AND COMPOUNDS | 2016年 / 682卷

关键词：

Vacuum brazing; Ti(C; N)-based cermets; Cu-Ag-Ti filler metal; Microstructure; Shear strength; STAINLESS-STEEL; MECHANICAL-PROPERTIES; CUTTING PERFORMANCE; INTERFACE STRUCTURE; BEHAVIOR; ALUMINA; COPPER; WC;

D O I：

10.1016/j.jallcom.2016.04.298

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

Microstructure and shear strength of Ti(C,N)-based cermet/Cu-30Ag-3Ti filler metal/W9Mo3Cr4V steel joints were investigated after brazing in vacuum at 870, 910, and 950 degrees C for 20 min, and 910 degrees C for 10, 20, 30 and 40 min. The reaction layer of Cu-Ni-Ti solid solution between cermet and filler metal was difficult to form during brazing at 870 degrees C, leading to very low shear strength of joints. During brazing at 910 degrees C, Cu-Ni-Ti solid solution was formed between cermet and filler metal, and it became thick with the increase of holding time. Shear strength of joints reached a peak value for 30 min, due to the appropriate thickness of Cu-Ni-Ti solid solution. During brazing at 950 degrees C, Cu-Ni-Ti solid solution was formed and then grew on the whole along with Ag-based solid solution in filler metal, but was not formed between cermet and filler metal, thus deteriorating shear strength of joints. (C) 2016 Published by Elsevier B.V.

引用

页码：525 / 530

页数：6

共 35 条

[21] Brazing of hot isostatically pressed-Al2O3 to stainless steel (AISI 304L) by Mo-Mn route using 72Ag-28Cu braze [J].

Mishra, P ;

Sengupta, P ;

Athavale, SN ;

Pappachan, AL ;

Grover, AK ;

Suri, AK ;

Kale, GB ;

De, PK ;

Bhanumurthy, K .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2005, 36A (06) :1487-1494

[22]

Murray J., 1983, J PHASE EQUILIB, V4, P81, DOI [10.1007/BF02880329, DOI 10.1007/BF02880329]

[23] Nanostructure of wetting triple line in a Ag-Cu-Ti/Si3N4 reactive system [J].

Nomura, M ;

Iwamoto, C ;

Tanaka, SI .

ACTA MATERIALIA, 1999, 47 (02) :407-413

[24] Fe-Ti (iron-titanium) [J].

Okamoto, H .

JOURNAL OF PHASE EQUILIBRIA, 1996, 17 (04) :369-369

[25]

Rice J. P., 2002, Ceramic Engineering and Science Proceedings, V23, P809

[26]

Subramanian PR., 1993, J PHASE EQUILIB, V14, P62, DOI [DOI 10.1007/BF02652162, 10.1007/BF02652162]

[27] Diffusion bonding of aluminium oxide to stainless steel using stress relief interlayers [J].

Travessa, D ;

Ferrante, M ;

den Ouden, G .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2002, 337 (1-2) :287-296

[28]

Vianco PT, 2003, WELD J, V82, p268S

[29] Interface structure and mechanical properties of Ti(C,N)-based cermet and 17-4PH stainless steel joint brazed with nickel-base filler metal BNi-2 [J].

Wang, F. Z. ;

Wang, Q. Z. ;

Yu, B. H. ;

Xiao, B. L. ;

Ma, Z. Y. .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2011, 211 (11) :1804-1809

[30] Effect of Mo2C/(Mo2C + WC) weight ratio on the microstructure and mechanical properties of Ti(C, N)-based cermet tool materials [J].

Xu, Qingzhong ;

Zhao, Jun ;

Ai, Xing ;

Qin, Wenzhen ;

Wang, Dawei ;

Huang, Weimin .

JOURNAL OF ALLOYS AND COMPOUNDS, 2015, 649 :885-890

← 1 2 3 4 →