Hydrophobicity of Polyacrylate Emulsion Film Enhanced by Introduction of Nano-SiO2 and Fluorine

This study proposes to utilize modified Nano-SiO2/fluorinated polyacrylate emulsion that was synthesized with a semi-continuous starved seed emulsion polymerization to improve the hydrophobicity, thermal stability, and UV-Vis absorption of polyacrylate emulsion film. To verify the proposed method, a series inspection had been conducted to investigate the features of the emulsion film. The morphological analysis indicated that Nano-SiO2 was surrounded by a silane molecule after modification, which can efficiently prevent silica nanoparticles from aggregating. Fourier transform infrared spectra confirmed that modified SiO2 and dodecafluoroheptyl methacrylate (DFMA) were successfully introduced to the copolymer latex. The particle size of latex increased with the introduction of modified Nano-SiO2 and DFMA. UV-Vis absorption spectra revealed that modified silicon nanoparticles can improve the ultraviolet shielding effect obviously. X-ray photoelectron spectroscopy illustrated that the film-air interface was richer in fluorine than film section and the glass side. The contact angle of modified Nano-SiO2/fluorinated polyacrylate emulsion containing 3 wt % DFMA was 112 degrees, slightly lower than double that of polyacrylate emulsion, indicating composite emulsion films possess better hydrophobicity. These results suggest that introducing modified Nano-SiO2 and fluorine into polyacrylate emulsion can significantly enhance the thermal stability of emulsion films.