Preparation of nanocrystalline NiAl compounds and composites by mechanical alloying

被引：6

作者：

Guo, JT ^{[1
]}

Du, XH ^{[1
]}

Zhou, LZ ^{[1
]}

机构：

[1] Chinese Acad Sci, Superalloys Div, Met Res Inst, Shenyang 110016, Peoples R China

来源：

PRICM 5: THE FIFTH PACIFIC RIM INTERNATIONAL CONFERENCE ON ADVANCED MATERIALS AND PROCESSING, PTS 1-5 | 2005年 / 475-479卷

关键词：

NiAl based alloys; mechanical alloying; nanocrystalline; mechanical properties;

D O I：

10.4028/www.scientific.net/MSF.475-479.749

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

During the past ten years, mechanical alloying/ball milling has been employed to successfully synthesize nanocrystalline NiAl intermetallic compounds (NiAl, NiAl (Cr,Co,Ti,Fe)) and composites (NiAl-TiC, NiAl-TiB2, NiAl-HfC, NiAl-HfB2) in our group, namely, by means of self-sustained reaction. During the mechanical alloying process, an abrupt temperature rise has been observed. The large heat release from the formation of NiAl, as well as HfC, HfB2, TiC, TiB2 compounds is suggested to be the driven force of the self-sustained reaction. It is interested to observe that nanocrystalline NiAl exhibits very well microstructure stability during high temperature annealing. The alloying additions can decrease reaction rate and prolong the reaction time. With the increase of alloying additions, supersaturated solid solution even amorphization of NiAl has been formed. The nanocrystalline NiAl compounds show a rise of the compressive strength and the ductility at room temperature compared with that of the cast coarse crystalline compound.

引用

页码：749 / 754

页数：6

共 28 条

[1]

ATZRNON M, 1990, PHYS REV LETT, V64, P487

[2]

BENJAMIN JS, 1976, SCI AM, V40, P234

[3]

DEEVI SC, 1911, J MATER SCI, V26, P3343

[4] NANOCRYSTALLINE MATERIALS [J].

BIRRINGER, R .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1989, 117 :33-43

[5] Microstructure, interface and mechanical property of the DS NiAl/Cr(Mo,Hf) composite [J].

Guo, JT ;

Cui, CY ;

Chen, YX ;

Li, DX ;

Ye, HQ .

INTERMETALLICS, 2001, 9 (04) :287-297

[6] RECRYSTALLIZATION AND GRAIN-GROWTH IN NIAL [J].

HAFF, GR ;

SCHULSON, EM .

METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1982, 13 (09) :1563-1566

[7] DIFFUSION OF BORON IN THE ORDERED FE-26AT-PERCENT-AL ALLOY [J].

HASAKA, M ;

MORIMURA, T ;

KONDO, S ;

UCHIYAMA, Y ;

HISATSUNE, K .

SCRIPTA METALLURGICA ET MATERIALIA, 1993, 29 (07) :967-970

[8] MECHANICALLY ALLOYED NI50TI50 AND ITS TRANSFORMATION BY THERMAL TREATMENTS [J].

ITSUKAICHI, T ;

OHURA, S ;

CABANASMORENO, JG ;

UMEMOTO, M ;

OKANE, I .

JOURNAL OF MATERIALS SCIENCE, 1994, 29 (06) :1481-1486

[9] CERAMICS DUCTILE AT LOW-TEMPERATURE [J].

KARCH, J ;

BIRRINGER, R ;

GLEITER, H .

NATURE, 1987, 330 (6148) :556-558

[10] Overview paper no. 2. The synthesis and structure of nanocrystalline materials produced by mechanical attrition. A review [J].

Koch, C.C. .

Nanostructured Materials, 1993, 2 (02)

← 1 2 3 →