EXPERIMENTAL INVESTIGATION AND TAGUCHI OPTIMISATION OF DRILLING PROPERTIES ON TEAK WOOD REINFORCED EPOXY RESIN

The drilling properties of teak reinforced epoxy resin composite are explored in this work. The thrust force and temperature during the drilling process was found and optimised. Nine holes were drilled in accordance with L9 orthogonal array on Medium Density Fibre board and Teak wood reinforced epoxy composite board and the thrust force and temperature induced during drilling is measured. Drilling experiments were conducted using CNC Vertical drilling machine and the thrust force was measured using dynamometer and temperature using infra-red thermometer. The experiments were conducted with varying levels of spindle speed and feed rate and optimised using Taguchi optimisation. It was observed that higher thrust and temperature were observed while drilling teak wood composite due to the high mechanical strength of teak wood. The hard and brittle properties of the resin seemed to be more pronounced in the composite. The experimental results were optimised to find the best combination of input parameters for reduced thrust and temperature. When speed increases, thrust force decreases and temperature increases. When feed increases, thrust force increases and temperature decreases. Experimental findings encouragesto use teak wood reinforced epoxy resin as a substitute for the traditionally used Medium Density Fibre Board. The percentage of mixing of teak dust can be increased with various resin combinations to arrive at the best suitable combination for obtaining optimal mechanical properties.