Chromium and tungsten carbide coating of AISI D3 steel by a thermoreactive diffusion process

被引:0
作者
Topuz, A [1 ]
Mollaoglu, H [1 ]
机构
[1] Yildiz Tech Univ, Dept Met & Mat Engn, TR-34210 Istanbul, Turkey
来源
PRAKTISCHE METALLOGRAPHIE-PRACTICAL METALLOGRAPHY | 2003年 / 40卷 / 12期
关键词
chromium carbide; tungsten carbide; iron alloys; adhesion; pack diffusion coatings;
D O I
暂无
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
In this study AISI D3 steel surfaces were coated with chromium and tungsten carbide by using thermoreactive diffusion process. The chromium carbide coating process was carried out at 1000degreesC and 1100degreesC for 5 hours. Chromium carbide coating process was carried out at two different compositions. One of the compositions includes powder of pure chromium, inert filler (Al2O3), carbon containing compound (C12H10), activator (NH4Cl) and the other includes powder of ferrochromium, Al2O3, C8H10 and NH4Cl. After coating process some of the chromium carbide coated specimens were quenched in water and oil. Tungsten carbide coating process was carried out at 1000degreesC for 5 hours in contact with powder of tungsten Al2O3, C12H10 and NH4Cl. At the end of thermally activated process, the carbide coatings were examined by means of optical microscopy and SEM, micro hardness measurement and X Ray diffraction. Also the adhesion of the carbide layers was examined by Rockwell-C adhesion test.
引用
收藏
页码:602 / 613
页数:12
相关论文
共 7 条
[1]  
ALTAR F, 1996, SURFACE COATINGS TEC, V78, P78
[2]  
[Anonymous], 1991, ASM HDB
[3]  
*DIN, 1993, ROCKW EINDR CHAR DUN, P212
[4]   Evaluation of PVD nitride coatings, using impact, scratch and Rockwell-C adhesion tests [J].
Heinke, W ;
Leyland, A ;
Matthews, A ;
Berg, G ;
Friedrich, C ;
Broszeit, E .
THIN SOLID FILMS, 1995, 270 (1-2) :431-438
[5]  
JURKOV I, 1998, COMPOSITION DEPOSITI
[6]  
REYNOLDSON RW, 1993, HEAT TREATMENT FLUID, P448
[7]  
Topuz A, 1999, PRAKT METALLOGR-PR M, V36, P5