Production of viscosity improvers for PVC

被引：1

作者：

Bostanci, T ^{[1
]}

Güner, FS

Erciyes, T

机构：

[1] Istanbul Tech Univ, Mat Sci & Engn Dept, TR-34469 Istanbul, Turkey

[2] Istanbul Tech Univ, Dept Chem Engn, TR-34469 Istanbul, Turkey

来源：

MACROMOLECULAR SYMPOSIA | 2005年 / 228卷

关键词：

additives; lubricants; mixer; PVC;

D O I：

10.1002/masy.200551021

中图分类号：

O63 [高分子化学（高聚物）];

学科分类号：

070305 ; 080501 ; 081704 ;

摘要：

Some oil-based samples having oxygen, ester, amide, acid and/or hydroxyl structure were prepared for using as lubricants in PVC extrusion. After characterization studies, all samples were tested in PVC formulation using Brabender W50 EHT Lab-Station mixer and extruder. The results were compared with that of a commercial product. From the mixer results, it can be noted that energy consumption was lowered for samples containing acid and amide structures. Surface roughness and opacity of the products were improved when the extruder screw speed was increased from 20 rpm to 60 rpm.

引用

页码：237 / 243

页数：7

共 50 条

[1] Viscosity effects in rigid PVC
Berard, MT
ANTEC 2000: SOCIETY OF PLASTICS ENGINEERS TECHNICAL PAPERS, CONFERENCE PROCEEDINGS, VOLS I-III, 2000, : 3397 - 3401
[2] Core-Crosslinked Star Copolymers as Viscosity Index Improvers for Lubricants
Sparnacci, Katia
Frison, Tommaso
Podda, Edoardo
Antonioli, Diego
Laus, Michele
Notari, Marcello
Assanelli, Giulio
Atzeni, Marco
Merlini, Gianfranco
Po, Riccardo
ACS APPLIED POLYMER MATERIALS, 2022, 4 (12): : 8722 - 8730
[3] Epoxidized Oleic Acid-Based Polymethacrylates as Viscosity Index Improvers
Lomege, Juliette
Lapinte, Vincent
Negrell, Claire
Robin, Jean-Jacques
Caillol, Sylvain
JOURNAL OF THE AMERICAN OIL CHEMISTS SOCIETY, 2019, 96 (04) : 467 - 478
[4] Synthesis and evaluation of viscosity index improvers and pour point depressant for lube oil
Nassar, A. M.
PETROLEUM SCIENCE AND TECHNOLOGY, 2008, 26 (05) : 523 - 531
[5] Technical progresses for PVC production
Saeki, Y
Emura, T
PROGRESS IN POLYMER SCIENCE, 2002, 27 (10) : 2055 - 2131
[6] Synthesis and Characterization of Novel Terpolymers as Viscosity Index Improvers Using Industrial Waste for Iraqi Lubricating Oil
AL-Malki, Ziyad Tarik
Khalaf, Moayad Naeem
INDONESIAN JOURNAL OF CHEMISTRY, 2024, 24 (03) : 835 - 844
[7] Influence of Structure and Property of Plasticizers on Viscosity and Aging Process of PVC Plastisols
Xu Guo-min
Ji Yu-bi
Yang Zhao
Tan Hong
ADVANCED MATERIALS AND ENGINEERING APPLICATIONS, 2012, 161 : 15 - 20
[8] Elion Chem to Add PVC Production Line
China Chemical Reporter, 2010, 21 (13) : 31 - 31
[9] Continuous Extrusion Production of Microcellular Rigid PVC
Diaz, Carlos A.
Matuana, Laurent M.
JOURNAL OF VINYL & ADDITIVE TECHNOLOGY, 2009, 15 (04): : 211 - 218
[10] 200 000 T/A PVC Project Starts Production
China Chemical Reporter, 2007, (29) : 11 - 11

← 1 2 3 4 5 →