Influence of fibre stretching on the microstructure of self-reinforced poly(ethylene terephthalate) composite

被引:8
|
作者
Jerpdal, Lars [1 ,2 ]
Stahlberg, Daniel [1 ]
Akermo, Malin [2 ]
机构
[1] Scania CV AB, Sodertalje, Sweden
[2] Royal Inst Technol, Aeronaut & Vehicle Engn, Teknikringen 8, SE-10044 Stockholm, Sweden
关键词
Self-reinforced polymer composite; poly(ethylene terephthalate); microstructural analysis; mechanical properties; ETHYLENE TEREPHTHALATE FIBERS; REFLECTION FTIR SPECTROSCOPY; MOLECULAR-ORIENTATION; PET YARNS; DRAWN POLY(ETHYLENE-TEREPHTHALATE); INFRARED-SPECTROSCOPY; BIAXIAL ORIENTATION; POLYMER COMPOSITES; SURFACE-STRUCTURE; SHRINKAGE;
D O I
10.1177/0731684416662328
中图分类号
TB33 [复合材料];
学科分类号
摘要
Self-reinforced poly(ethylene terephthalate) laminates were prepared from woven fabric by compression moulding. The fabric was stretched to different degrees during heating before hot consolidation to simulate a manufacturing process where the material is stretched through forming. High tenacity poly(ethylene terephthalate) fibres with different degrees of stretching were prepared for a comparison to laminates. Tensile tests were made to characterize mechanical properties, while dynamical mechanical analysis, differential scanning calorimetry, FTIR spectroscopy and X-ray diffraction analysis were employed to study microstructural changes caused by the stretching. Tensile tests show that 13% stretching of the fabric increases the laminate tensile stiffness by 34%. However, same degree of stretching for pure fibres increases the fibre tensile stiffness by 111%. Crystallinity and molecular conformations are not influenced by stretching while shrinkage upon heating increases with degree of stretching. Shrinkage is known to be related to disorientation of non-crystalline regions whereof the conclusion from this study is that the increased tensile properties are due to orientation of the non-crystalline regions of the fibre.
引用
收藏
页码:1634 / 1641
页数:8
相关论文
共 50 条
  • [21] Poly(ethylene terephthalate) fibre with birefringence of 0.26
    Gupta, V.B.
    Sett, S.K.
    Deorukhkar, D.D.
    Polymer communications Guildford, 1989, 30 (11): : 341 - 343
  • [22] Blends of poly(ethylene terephthalate) and epoxy as matrix material for continuous fibre reinforced composites
    Saalbrink, A
    Mureau, M
    Peijs, T
    PLASTICS RUBBER AND COMPOSITES, 2001, 30 (05) : 213 - 221
  • [23] Influence of microstructure evolution on mechanical strength of blown poly(ethylene terephthalate)
    Chevalier, L
    PLASTICS RUBBER AND COMPOSITES, 1999, 28 (08) : 385 - 392
  • [24] Influence of microstructure evolution on mechanical strength of blown poly(ethylene terephthalate)
    Lab. Mecanique Technol. ENS-Cachan, 61 avenue du Président Wilson, 94235 Cachan Cedex, France
    Plast Rubber Compos Process Appl, 8 (385-392):
  • [25] CHAIN STRETCHING IN A POLY(ETHYLENE-TEREPHTHALATE) FIBER
    YOUNG, RJ
    YEH, WY
    POLYMER, 1994, 35 (18) : 3844 - 3847
  • [26] The bifunctionality of poly[(R)-3-hydroxybutyrate] in self-reinforced composite materials
    Jurczyk, Sebastian
    Wlodarczyk, Jakub
    Kawalec, Michai
    Janeczek, Henryk
    Michalak, Michal
    Sobota, Michal
    POLYMER TESTING, 2017, 63 : 614 - 620
  • [28] INFLUENCE OF WARM STRETCHING ON GLASS-TRANSITION TEMPERATURE OF POLY-(ETHYLENE TEREPHTHALATE)
    LATROUS, K
    CAVROT, JP
    RIETSCH, F
    MAKROMOLEKULARE CHEMIE-RAPID COMMUNICATIONS, 1981, 2 (02): : 145 - 148
  • [29] Bending and fracture toughness of woven self-reinforced composite poly(methyl methacrylate)
    Wright, DD
    Lautenschlager, EP
    Gilbert, JL
    JOURNAL OF BIOMEDICAL MATERIALS RESEARCH, 1997, 36 (04): : 441 - 453
  • [30] Microstructure of amorphous and crystalline poly(ethylene terephthalate)
    The Univ of Toledo, Toledo, United States
    J Appl Polym Sci, 10 (1965-1976):