The environment-induced cracking of as-cold rolled Ni3(Si,Ti) and Ni3(Si,Ti) with 2Mo in sodium chloride solutions

被引：2

作者：

Priyotomo, Gadang ^{[1
]}

Wagle, Sanat ^{[2
]}

Okitsu, Kenji ^{[3
]}

Iwase, Akihiro ^{[3
]}

Kaneno, Yasuyuki ^{[3
]}

Nishimura, Rokuro ^{[3
]}

Takasugi, Takayuki ^{[3
]}

机构：

[1] Indonesian Inst Sci, Kawasan PUSPIPTEK, Res Ctr Met & Mat, Tangerang Selatan 15314, Banten, Indonesia

[2] UiT Arctic Univ Norway, Dept Phys & Technol, N-9037 Tromso, Norway

[3] Osaka Prefecture Univ, Grad Sch Engn, Dept Mat Sci, Sakai, Osaka 5998531, Japan

来源：

JOURNAL OF ALLOYS AND COMPOUNDS | 2015年 / 639卷

关键词：

Intermetallics; SEM; Hydrogen embrittlement; Stress corrosion; AUSTENITIC STAINLESS-STEELS; GRAIN-BOUNDARY SEGREGATION; STRESS-CORROSION CRACKING; HYDROGEN EMBRITTLEMENT; HYDRIDE FORMATION; ACID-SOLUTIONS; BEHAVIOR; NICKEL; TITANIUM; NI3(SI;

D O I：

10.1016/j.jallcom.2015.03.202

中图分类号：

O64 [物理化学（理论化学）、化学物理学];

学科分类号：

070304 ; 081704 ;

摘要：

The environment-induced cracking (EIC) of as cold-rolled Ni-3(Si, Ti) and Ni-3(Si, Ti) with 2Mo has been investigated as functions of applied stress, chloride ion concentration, test temperature, and pH by using a constant load method in NaCl solutions. The EIC susceptibility of both intermetallic compounds increased with increasing Cl ion concentration and test temperature; and increased with decreasing pH. Both intermetallic compounds had the same transgranular fracture appearance and the relationship between log t(f) (time to failure) and log l(ss) (steady state elongation rate) became the identical straight line irrespective of applied stress, Cl ion concentration, test temperature, and pH, which means that l(ss) becomes a relevant parameter for predicting t(f). The EIC susceptibility of Ni-3(Si, Ti) with 2Mo was lower than that of Ni-3(Si, Ti), which showed the beneficial effect of Mo. From the results obtained, EIC of both intermetallic compounds was presumed to take place by hydrogen embrittlement (HE). (C) 2015 Elsevier B.V. All rights reserved.