Study on corrosion fatigue behavior and mechanism of 6005A aluminum alloy and welded joint

被引：8
|
作者：
Sun, Xiaoguang [1 ,2 ]
Xu, Xuexu [1 ]
Wang, Zihan [1 ]
Liu, Zhiyong [1 ]
机构：
[1] Univ Sci & Technol Beijing, Inst Adv Mat & Technol, Beijing, Peoples R China
[2] CRRC Qingdao Sifang Rolling Stock Res Inst Co Ltd, Qingdao, Peoples R China
来源：
ANTI-CORROSION METHODS AND MATERIALS | 2021年 / 68卷 / 04期
基金：
中国国家自然科学基金;
关键词：
Welded joint; Aluminum alloy; Corrosion fatigue; 6005A; WEATHERING STEEL; INCLUSIONS;
D O I：
10.1108/ACMM-04-2021-2471
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Purpose The purpose of this paper is to determine the corrosion fatigue behavior and mechanism of 6005A aluminum alloy and welded joint. Design/methodology/approach Electron back-scattered diffraction (EBSD) were adopted to characterize the microstructure of 6005A aluminum alloy and welded joint. Through potentiodynamic polarization, electrochemical impedance spectroscopy (EIS) and corrosion fatigue experiments, the corrosion fatigue behavior and mechanism of 6005A aluminum alloy base metal and welded joint were studied. Findings The results show that the corrosion fatigue crack initiation of 6005A aluminum alloy base metal and welded joint is mainly caused by the preferential anodic dissolution and hydrogen concentration in the areas with inclusions and welding defects. Originality/value The research is an originality study on the corrosion fatigue behavior and mechanism of 6005A aluminum alloy and welded joint.
引用
收藏
页码：302 / 309
页数：8
相关论文
共 50 条
  • [21] The Microstructure and Mechanical Properties of 5083, 6005A and 7N01 Aluminum Alloy Gas Metal Arc-Welded Joints for High-Speed Train: A Comparative Study
    Wu, Laijun
    Yang, Biao
    Han, Xiaohui
    Ma, Guolong
    Xu, Bingxiao
    Liu, Yuhang
    Song, Xiaoguo
    Tan, Caiwang
    METALS, 2022, 12 (02)
  • [22] Fatigue corrosion behavior of friction-welded stainless and carbon steel dissimilar joint
    Benedetti, Matteo
    Orempuller, Mattia
    Russo, Francesca
    Fontanari, Vigilio
    Rossi, Stefano
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2023, 46 (02) : 555 - 573
  • [23] Microstructure and corrosion behavior of bobbin tool friction stir welded 2219 aluminum alloy
    Shao, Minghao
    Wang, Caimei
    Zhang, Hua
    Zhang, Jian
    Liu, Debo
    Wang, Feifan
    Ji, Yajuan
    Chen, Gaoqiang
    MATERIALS CHARACTERIZATION, 2022, 192
  • [24] Study on the Dimensional Stability of Aluminum Alloy Welded Joint under Space Thermal Cycling Conditions
    Jin, Cheng
    Niu, Jitai
    Shi, Chunyuan
    APPLIED MECHANICS AND MECHANICAL ENGINEERING, PTS 1-3, 2010, 29-32 : 1850 - +
  • [25] Influence of stress ratios on fatigue strength of A6005C-T5 aluminum alloy and its friction stir welded joints
    Hagisawa, Nobuyasu
    Okura, Ichiro
    Doboku Gakkai Ronbunshuu A, 2009, 65 (01) : 117 - 122
  • [26] Fatigue strength optimisation of friction stir welded A6005-T5 alloy sheets
    Jung, S. P.
    Park, T. W.
    Kim, Y. G.
    SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2010, 15 (06) : 473 - 478
  • [27] Fatigue strength of aluminum 5083 welded joint with longitudinal fillet welded gusset
    Jia, Fayong
    Huo, Lixing
    Wu, Bing
    Wang, Dongpo
    Jixie Gongcheng Xuebao/Chinese Journal of Mechanical Engineering, 2005, 41 (08): : 199 - 202+207
  • [28] Corrosion fatigue behavior of AA 7020 alloy in seawater
    Yurdgulu, Halil Ibrahim
    Sadeler, Recep
    Yilmaz, Hasan
    Koc, Baris
    MATERIALS TESTING, 2023, 65 (05) : 743 - 752
  • [29] Study of the Corrosion Mechanism and Corrosion Inhibition of 2024 Aluminum Alloy by SKPFM Technique
    Yasakau, K. A.
    Zheludkevich, M. L.
    Ferreira, M. G. S.
    ADVANCED MATERIALS FORUM IV, 2008, 587-588 : 405 - 409
  • [30] The corrosion behavior of marine aluminum alloy MIG welded joints in a simulated tropical marine atmosphere
    Gong, Lihua
    Guo, Weimin
    Pan, Feng
    MATERIALS TESTING, 2021, 63 (02) : 151 - 156
12345